Na 2 S Treatment and Coherent Interface Modification of the Li-Rich Cathode to Address Capacity and Voltage Decay
Kanghui Hu,Genpin Lv,Jun Zhang,Xiaodong Guo,Zhenguo Wu,Wei Xiang,Xipeng Lan,Kun Zhou,Peng Xu,Liang Zhang
DOI: https://doi.org/10.1021/acsami.0c08797
2020-09-03
Abstract:Li-rich and Mn-based layered oxides are the most promising candidates for next-generation high energy density cathode materials. However, inherent problems including poor rate performance, continuous capacity degradation, and voltage fading hinder their commercial utilization. Herein, a lattice- and interfacial-modified Li<sub>1.2</sub>Mn<sub>0.54</sub>Co<sub>0.13</sub>Ni<sub>0.13</sub>O<sub>2</sub> with a pristine-layered bulk structure, Na- and S-doped transition phase, and epitaxially grown Na<sub>2</sub>Mn (SO<sub>4</sub>)<sub>2</sub> (<i>C</i>2/<i>c</i> symmetry) layer were constructed by Na<sub>2</sub>S treatment. The monoclinic Na<sub>2</sub>Mn(SO<sub>4</sub>)<sub>2</sub> not only acts as an interface protective layer, alleviating the harmful electrode–electrolyte reactions, but also promotes formation of oxygen vacancy in the layered structure, enhancing reversibility of oxygen redox. The Na and S surface lattice doping leads to enhanced Li<sup>+</sup> diffusion and alleviates the chance of oxygen release. With the positive effects provided by the stable interfacial layer and lattice modification, the modified cathodes with moderate Na<sub>2</sub>S treatment shows alleviated capacity and voltage decay and enhanced electrochemical kinetics. Especially, the washed cathode with 3 wt % Na<sub>2</sub>S treatment delivers a discharge specific capacity of 305 at 0.1 C and 219 mA h g<sup>–1</sup> at 1 C, as well as 93.15% capacity retention and 88.20% voltage retention after 200 cycles at 1 C.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c08797?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c08797</a>.Rietveld refinement patterns using powder XRD of LMCN, LMCN-NS1, LMCN-NS3, LMCN-NS6, and WLMCN-NS3 samples; summary of structural refinement of the samples by a Rietveld method; HRTEM and FFT images of LMCN-NS3; the cross-section SEM image and corresponding Ni, Co, Mn, Na, S, and O distribution on the cross-sectioned particle for LMCN-NS3; EPR spectra of LMCN and LMCN-NS3; initial charge/discharge profiles of LMCN, LMCN-NS1, LMCN-NS3, and LMCN-NS6 at 0.1 C; cyclic performance of LMCN, LMCN-NS1, LMCN-NS3, and LMCN-NS6 at 1 C; initial charge/discharge profiles of LMCN, LMCN-N3, LMCN-S3, and LMCN-NS3 at 0.1 C; rate capability of LMCN, LMCN-N3, LMCN-S3, and LMCN-NS3; cyclic performance of LMCN, LMCN-N3, LMCN-S3, and LMCN-NS3 at 1 C; average voltage of discharging process for LMCN, LMCN-NS3, and W LMCN-NS3 at 1 C; XPS spectra of Mn 2p, Ni 2p, Co 2p, S 2p, Na 1s, and O 1s for LMCN and WLMCN-NS3 with different etching times; CV curves of the LMCN and WLMCN-NS3; and corresponding detailed data of <i>R</i><sub>s</sub>, <i>R</i><sub>ct</sub>, σ<sub>ω</sub>, and <i>D</i><sub>Li<sup>+</sup></sub> of the LMCN and WLMCN-NS3, respectively, for 1st and 300th (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c08797/suppl_file/am0c08797_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology