Abstract:Atmospheric acid leaching behaviour of scandium (Sc) in two different types of laterite nickel ore from Indonesia was investigated. Ore and leaching residue characterization was performed by XRD, FTIR, XPS, and SEM-EDX. Ore characterisation showed that the major minerals in limonitic laterite were goethite, magnetite, hematite, and saprolitic laterite mainly consisted of goethite, magnetite, lizardite, clinochlore. Sc in two different types of laterite nickel ore are distributed widely among minerals, but it mainly hosts in Al-bearing goethite and silicate minerals. Sc host minerals in limonitic and saprolitic laterite nickel ore are different. 84.27% and 59.86% of Sc in limonitic and saprolitic laterite could be leached under the experimental conditions of 3 mol/L H2SO4, 80℃ reaction temperature, leaching duration 3 h and liquid to solid ratio 6:1, respectively. The results show that Sc and Mn, Mg in limonitic laterite have similar dissolution characteristics because the extractions of Sc and Mn, Mg are linearly correlated. Sc in limonitic laterite is susceptible to acid attack and easier to be extracted than other metals except for Mn. Sc and Ni in saprolitic laterite have similar dissolution characteristics because Sc is not strongly related to metals other than Ni. Sc in saprolitic laterite is more difficult to extract than Mg and Ni, but it is easier to be leached than other metals. The dissolution kinetics was found to fit well to the shrinking core model with the diffusion through the product layer as the rate controlling step. Results of this research may assist in the development of a more efficient process for exacting Sc from laterite nickel ores.

The effect of pre-roasting on atmospheric sulfuric acid leaching of saprolitic laterites

Effect of Pre-Roasting on Leaching of Laterite

The effect of pre-roasting on nickel extraction from limonite ore by acid leaching method

Enhancement of Nickel Extraction from Laterite in Hydrochloride Acid Through Activated Roasting

Atmospheric Leaching Behavior and Kinetics Study of Roasted Laterite Ore

The Extraction of Valuable Metals and Phase Transformation and Formation Mechanism in Roasting-Water Leaching Process of Laterite with Ammonium Sulfate

Effect of Leaching Conditions on Leaching Rate of Rare Earth and Iron

Influence of thermal treatment on the kinetics of manganese leaching from laterite ore

Research on the effect of additive on selective reduction of the laterite ores with low nickel and high iron content

Phase Transformation and Dissolution Behavior of Pyrite in the Roasting-Sulfuric Acid Leaching Process of Vanadium-Bearing Stone Coal

Thermodynamics and Chloridizing Roasting Conditions of Laterite Through Ammonium Chloride

Physicochemical Factors Affecting Leaching of Laterite Ore in Hydrochloric Acid

Hydrochloric Acid Leaching of Laterite and Mineral Dissolution Mechanism Therein

Study on Thermal Decomposition Behavior and Roasting Desulfurization Mechanism of Jarosite Residue

Separation and Recovery of Iron and Nickel from Low-Grade Laterite Nickel Ore by Microwave Carbothermic Reduction Roasting

Influence of SiO2 and MgO on Extraction of Nickel and Cobalt from Laterite Ores by Sulfation Roasting Leaching Process

Reductive roasting of red mud with carbon and sulfuric acid dissolution of iron and aluminum: Transformation phases and leaching characteristics

Do ferrous iron-oxidizing acidophiles (Leptospirillum spp.) disturb aerobic bioleaching of laterite ores by sulfur-oxidizing acidophiles (Acidithiobacillus spp.)?

Study on leaching kinetics of laterite ore using hydrochloric acid

Study on the Migration and Release of Sulfur during the Oxidizing Roasting of High-Sulfur Iron Ore

Comparative atmospheric leaching characteristics of scandium in two different types of laterite nickel ore from Indonesia