Extraction of Nickel from Garnierite Laterite Ore Using Roasting and Magnetic Separation with Calcium Chloride and Iron Concentrate
Junhui Xiao,Wei Ding,Yang Peng,Tao Chen,Kai Zou,Zhen Wang
DOI: https://doi.org/10.3390/min10040352
IF: 2.5
2020-04-15
Minerals
Abstract:In this study, segregation roasting and magnetic separation are used to extract nickel from a garnierite laterite ore. The garnierite laterite ore containing 0.72% Ni, 0.029% Co, 8.65% Fe, 29.66% MgO, and 37.86% SiO2 was collected in the Mojiang area of China. Garnierite was the Ni-bearing mineral; the other main minerals were potash feldspar, forsterite, tremolite, halloysite, quartz, and kaolinite in the garnierite laterite ore. The iron phase transformations show that nickel is transformed from (Ni,Mg)O·SiO2·nH2O to a new nickel mineral phase dominated by [Ni]Fe solid solution; and iron changed from Fe2O3 and FeOOH to a new iron mineral phase dominated by metal Fe and Fe3O4 after segregation roasting. Ferronickel concentrate with Ni of 16.16%, Fe of 73.67%, and nickel recovery of 90.33% was obtained under the comprehensive conditions used: A roasting temperature of 1100 °C, a roasting time of 90 min, a calcium chloride dosage of 15%, an iron concentrate dosage of 30%, a coke dosage of 15%, a coke size of −1 + 0.5 mm, a magnetic separation grinding fineness of <45 μm occupying 90%, and a magnetic separation magnetic field intensity of H = 0.10 T. The main minerals in ferronickel concentrate are Fe, [Ni]Fe, Fe3O4, and a small amount of gangue minerals, such as CaO·SiO2 and CaO·Al2O3·SiO2.
geochemistry & geophysics,mineralogy,mining & mineral processing