Effects and Mechanism of Damp Milling on Selective Reduction of Lateritic Ore

Wang Xiaoping,Sun Tichang,Xu Chengyan,Zhao Yongqiang,Wu Xiaodan,Yan Gongjun

DOI: https://doi.org/10.3969/j.issn.1001-1250.2017.09.017

2017-01-01

Abstract:The process of reduction roasting followed by low-intensity magnetic separation are usually used to recover nickel and iron from laterite ores. In order to strengthen the selective reduction of nickel in laterite ore,the effect of damp mill-ings for the mixture of a laterite ore,coal as a reductant,and sodium sulfate as an additive on selective reduction of nickel in the sample ore and its mechanism were investigated. The results showed that:① Within the fineness range of damp millings, damp millings was favorable to strengthen the selective reduction. When the fineness of the mixture is increased from -0. 074 mm of 52. 00% to -0. 074 mm of 75. 49%,nickel grade of the Ni-Fe product is improved from 6. 58% to 9. 27%,and the grade of the Ni-Fe product increased from three levels to a specific pole,accompanied with nickel recovery rate increasing from 91. 56% to 95. 57% and differences in nickel and iron recovery rising from 54. 30% to 68. 52%.②Damp millings made the particle size of the sample be reduced and the fresh surface of the nickel ore was sufficiently exposed,making the sample ore, lignite,and sodium sulfate being fully mixed. It improved the contact reaction probability of target minerals,lignite and sodium sulfate,contributing to strengthening the selective reduction of nickel.③Damp milling had no obvious influence on mineral composition of the roasted ores but remarkably affect the microstructure of roasted ore,which promoted aggregation of the fine Ni-Fe particles and was beneficial to realize monomer dissociation for the Ni-Fe particles during subsequent magnetic separa-tion.④Sum of nickel and iron grades was only 80. 33% with damp milling for the mixture fineness at-0. 074 mm of 75. 49%, because there were intergrowth and mechanical impurity inclusion in the Ni-Fe product,and the phenomenon of carburization of ferronickel particles existed. The former can be reduced through a two-section grinding and low-intensity magnetic concentration process,but the latter is difficult to avoid.