The Influence of Layered Milling and Stress Relief Annealing on the Surface Quality of Magnesium Alloy Frame Parts
Rongjun Wang,Yang Huang,Weihua Ding,Zhi Chen,Pengchong Zhang,Qi Zhou,Hao Su
DOI: https://doi.org/10.1007/s11665-024-09837-1
IF: 2.3
2024-07-19
Journal of Materials Engineering and Performance
Abstract:Magnesium alloy is a lightweight, high-strength green metal material. However, during cutting processes, it is prone to generate high cutting temperatures and cutting forces, leading to workpiece deformation, which restricts the development of magnesium alloy frame components. Enhancing the dimensional stability and surface quality of magnesium alloy frame components, as well as improving their service performance, are critical issues that need to be addressed urgently. In this study, based on different standards required in practical production, layered milling combined with stress relief annealing schemes are investigated for various milling parameters. The results show that in layered milling, finishing machining has a greater impact on the surface quality of frame components compared to semi-finishing machining. Within the selected range of milling parameters, as the depth of finishing machining increases, the residual compressive stress on the surface of the frame component increases, the average surface roughness increases, and the surface morphology deteriorates. Both semi-finishing and finishing machining affect the surface hardness of the frame component, and after linear fitting, the surface hardness of the frame component decreases with the increase of total milling depth. Stress relief annealing can reduce the residual stress of magnesium alloy frame components, making the residual stress distribution of the frame component tend to be uniform. At the same time, it also reduces the surface hardness of the frame component and makes the surface hardness values of the workpiece tend to be evenly distributed.
materials science, multidisciplinary