Abstract:B4C/SiC (15 wt%) ceramic composite with 2 wt% carbon additive was fabricated via solid-phase pressureless sintering under an argon atmosphere for 60 min between 2100 degrees C and 2200 degrees C. The effects of the sintering temperature on the microstructure and mechanical properties of the B4C/SiC ceramic composites were studied in detail. The optimum values of the relative density, Vickers hardness, flexural strength, and fracture toughness of the B4C/SiC ceramic composite sintered at 2150 degrees C were 95.3%, 25.5 GPa, 296 MPa, and 2.81 MPa m(1/2), respectively. The microstructural investigations revealed that when the sintering temperature increases from 2100 degrees C to 2150 degrees C, sintered necks begin to grow and the densification zone increases. With sintering temperatures above 2150 degrees C, the grains grow rapidly such that the pores are not eliminated, causing the formation of large closed pores and resulting in a decrease in the relative density and mechanical properties of the B4C/SiC ceramic composite. The plate-like and irregular SiC grains are uniformly dispersed in the B4C matrix to inhibit B4C grain growth. The interface between SiC and B4C is clean and narrow, and the clean boundary suggests strong binding, which contributes to the mechanical properties of the B4C/SiC ceramic composite. At 2150 degrees C, the C additive undergoes significant crystallisation, forming lamellar structures with high aspect ratios, thereby promoting the pores in the ceramic composite to be discharged to the outside through volume diffusion to obtain a denser sintered body. The interface between B4C and graphite is a semi-coherent interface that increases the flexural strength with a low defect concentration. The main toughening mechanisms of the B4C/SiC ceramic composite are crack deflection and crack branching around the SiC grains and crack bridging by SiC grains in the wake of the crack tip. (C) 2019 Elsevier B.V. All rights reserved.

Effects of composite binder and sintering temperature on the microstructure, properties and reaction mechanism of polycrystalline diamond

Research Progress of Thermal Stability for Polycrystalline Diamond

Submicron Binderless Polycrystalline Diamond Sintering under Ultra-High Pressure

Effect of pressure on sintering behavior of polycrystalline diamond

Effects of carbon nanotubes and sintering parameters on microstructure and properties of PCD

High pressure and high temperature sintering of fine-grained PCD using bi-layered assembly

Preparation and Characterization of Carbide Particle-Toughened Si–B System of High Thermostability Polycrystalline Diamond by HPHT Sintering

Microstructural Evolution of Diamond-Based Composites at High Temperature and High Pressure

Discussion on the sintering problem of fine grain PCD

Sintering, microstructure, and mechanical properties of vitrified bond diamond composite

Influence of the Sintering Temperature on the Microstructure, Mechanical Properties and Densification Characteristics of (tib + TiC)/TC4 Composite

Synthesis and characterization of nPCD sintered from OLC and Microdiamond

Microstructure and Properties of Diamond/SiC Composites Via Hot Molding Forming and CVI Densifying

Experimental Studies of Submicron Polycrystalline Diamond Without Binder under High Pressure and Temperature

Effect of Sintering Temperature on Microstructure and Mechanical Properties of WC-Co-Ti<sub>3</sub>SiC<sub>2</sub> Cemented Carbides

Sintering Process of Polycrystalline Diamond Compact under High Pressure

Effect of Sintering Temperature on the Mechanical Properties and Microstructures of Pressureless-Sintered B4C/SiC Ceramic Composite with Carbon Additive

A Study on the Microstructure of Polycrystalline Diamond Composite (PDC) for Valves

Effect of Diamond Content on Microstructure and Properties of Diamond/sic Composites Prepared by Tape-Casting and CVI Process

Progress to Electrical Properties of Diamond-Sic Composites under High Pressure and High Temperature

High pressure sintering behavior of polycrystalline diamond with tungsten