Abstract:Abstract As the crucial structure in the pressure boundary of the steam generator in the high-temperature gas-cooled reactor (HTGR), it is essential to investigate the microstructure of T22/800H dissimilar metal weld (DMW) under thermal cycling. This is especially critical in the context of rapid temperature fluctuations under extreme conditions, which are likely to inflict irreparable damage on the material’s microstructure, thus posing a severe threat to the service life of the DMW. T22 and 800H base metal (BM) were welded by tungsten inert gas (TIG) welding, filling with UNS N06082 inserts. To investigate the impact of thermal cycling under extreme conditions on the microstructure of DWM, and to accelerate the evolution of microscopic phenomena, simulated thermal cycling tests were carried out at 500°C with a holding time of 1 hour per cycle and 300 cycles at two ramp-up/down rates of 3°C/min and 8°C/min between room temperature and 500°C, respectively, much more serious than the temperature evolution in start-ups and shutdowns during the operation of HTGR. Characterization of the microstructure of three typical failure-prone areas of T22/800H DMWs, namely the T22 base material (BM), the T22 heat-affected zone (HAZ) and the T22/WM fusion zone by optical microscopy (OM), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS), compared with that of the as-welded. It is obtained that limited cavities formed at the interface of T22 BM and the weld fusion zone (FZ), due to the prominent difference of thermal expansion, which contributes to the creep and fatigue, especially in the thermal cycling. Some cavities were also found in the fine-grained heat-affected zone (FGHAZ) of T22, ranging from 100 to 700nm in size. It is predicted that the cavities in FGHAZ were resulted from stress relief without preheat and post-weld heat treatment during the manufacturing of T22/800H DMWs. In addition, a mount of cavities, less than 100nm in size, were observed in the T22 BM during the thermal cycling test at 8°C/min; meanwhile, there were also some cavities, ranging from 100 to 300nm, found in the coarse-grained heat-affected zone (CGHAZ). It is supposed that the differences of thermal-physical properties, such as thermal expansion and hardness, make sense for the small cavities under thermal cycling. Sharp notches resulted from oxidization and thermal stress were found at the interfaces between T22 BM and weld metal, except for specimens without simulated thermal cycling.

Effect of high temperature service on the complex through-wall microstructure of centrifugally cast HP40 reformer tube

Effect of on-site service for 16,000 and 38,000 h on microstructure and mechanical properties of austenitic steel HR3C reheater tubes

An Investigation of the Effect of High-Temperature Cyclic Straining and Creep Loading on Tensile Mechanical Properties of GH4145/SQ Alloy

Experimental and simulative failure analysis of reformer furnace outlet manifolds serviced in aromatic plant

Weldability and Damage Evaluations of Fresh-to-Aged Reformer Furnace Tubes

Structural and Mechanical Characterization of Service Exposed 2.25Cr–1Mo Steel

Microstructure Impacts on Mechanical Properties in a High Temperature Austenitic Stainless Steel

Impact of Hot Bending on the High-Temperature Performance and Hydrogen Damage of 2.25Cr-1Mo-0.25v Steel

Investigation of damage on FeCr26Ni36Co15W5 alloy reduction furnace tube during service

Microstructural Evolution of TP347H After Post Weld Heat Treatment and Aging

Microstructure-Property Relationship and Embrittlement Mechanism of HR3C Steel with High-Temperature Service of 65000 h

High-temperature corrosion data and mechanisms for T122, Super304H and HR3C after 15 years in 1000MW ultra-supercritical power plant

High-Temperature Tensile and Creep Behavior in a CrMoV Steel and Weld Metal

Research of Welding Effect on Creep Damage of High Temperature Furnace Tubes

Effect of Annealing Temperature on microstructure and properties of the Microtubes for GH4169 alloy

Failure analysis of oil refinery heater treater's fractured fire tube

High-Temperature Degradation and Protection of Ferritic and Austenitic Steels in Steam Generators

Damage Analysis of In-Service Ethylene Cracking Furnace Tubes Using Small Punch Test

Effect of Thermal Cycling on the Microstructure of Nuclear Grade Dissimilar Metal Weld

Effect of Microstructural Evolution and Mechanical Properties of Haynes 230 Superalloy During Long-Term Aging at 700 °C

An Investigation of the Embrittlement in X20crmov12.1 Power Plant Steel after Long-Term Service Exposure at Elevated Temperature