Abstract:This work investigates the heterogeneous deformation and failure of HR3C austenitic stainless steel welded joints at room and typical service temperatures. Such types of welded joints are widely used in the new generation of fossil fuel power stations and are known to suffer from premature high temperature failure. Observation of in-service failures revealed that cracks may nucleate either in the heat affected zone or in the weld metal. The main objective of this work is to identify the local microstructural conditions and stress–strain fields responsible for both ductile failure and micro-crack nucleation within the weldment at low and high temperatures, respectively. To that purpose, a novel multi-scale micromechanics-based modelling framework is proposed. It relies on representative weld microstructure models digitally reconstructed from EBSD measurements, and dislocation density-based crystal plasticity models to describe the behaviour of individual grains in each weld region. A novel thermo-dynamically consistent relation for the configuration stored energy per unit volume is derived from the crystal plasticity framework. The single crystal models are calibrated and validated from a combination of uniaxial tensile tests on cross-weld specimens using high resolution digital image correlation techniques, representative volume elements of the polycrystals at the macro-scale, as well as micropillar compression tests at the scale of the individual grains. Predictions of heterogeneous inelastic deformation fields within the weldment at both 22 °C and 665 °C, and of micropillar compression behaviour of the individual weld single crystal phases are consistent with experimental data. The experimentally observed ductile failure of the weld metal at room temperature is successfully predicted using a Gurson-type void nucleation, growth and coalescence constitutive model. The suitability of the stored strain energy density and the accumulated plastic strain as crack initiation/creep failure indicators is investigated. It was found that predicted creep lifetimes with either indicator were very similar, and that they were relatively accurate for low stress levels.

Weldability and Damage Evaluations of Fresh-to-Aged Reformer Furnace Tubes

Effect of Long-Term Aging on Microstructure and Local Behavior in the Heat-Affected Zone of a Ni–Cr–Mo–V Steel Welded Joint

Research of Welding Effect on Creep Damage of High Temperature Furnace Tubes

Remaining creep properties and fracture behaviour of P92 steel welded joint under prior low cycle fatigue loading

Addressing the Abnormal Grain Coarsening During Post-Weld Heat Treatment of TIG Repair Welded Joint of Sand-Cast Mg-Y-RE-Zr Alloy

EFFECT OF THERMAL AGING TREATMENT ON MICROSTRUCTURE EVOLUTION AND MECHANICAL PROPERTIES DEVELOPMENT IN A NI-CR-MO-V WELD METAL

Micromechanical Study of Heterogenous Deformation of Austenitic Stainless Steel Welded Joints at Different Temperatures

Residual Life Assessment on the Reformer Tube Welded with Serviced and New HP.Nb Material

Effect of Post-Welding Aging Treatment on the Microstructure and High-Temperature Properties of Inertia Friction Welded GH4065A Joint

Microstructure and mechanical properties characterization of aged and repair welded Alloy 617M

Investigation of damage on FeCr26Ni36Co15W5 alloy reduction furnace tube during service

The Relationship Between Micro-damage of Furnace Tube in Service and Weldability

Influence of Microstructure Evolution on Reheat Cracking Behavior of T23 Steel Weld Joint

Study on Microstructure and Properties of Dissimilar Steel Welded Joints of FV520(B)

Microstructural/mechanical Characterizations of Electron Beam Welded IN738LC Joint after Post-Weld Heat Treatment

Influence of Aging Treatment on the Microstructure and Mechanical Properties of T92/Super 304H Dissimilar Metal Welds

Damage Analysis of In-Service Ethylene Cracking Furnace Tubes Using Small Punch Test

Microstructures and Mechanical Properties of Electron Beam Welded CuCrZr/Inconel/316L Tube-to-tube Junctions for WEST Project

Effect of long-term aging on near-threshold fatigue crack growth of Ni–Cr–Mo–V steel welds

Micro-mechanics investigation of heterogeneous deformation fields and crack initiation driven by the local stored energy density in austenitic stainless steel welded joints

Aging Treatment on the Microstructures and Mechanical Properties of New Groove T92/Super 304H Dissimilar Steel Joints