Abstract:Nano-boron nitride (h-BN) has excellent physical and mechanical properties. Due to its stable chemical performance, the improvement effect on the properties of cement-based materials was limited. Therefore, the chemical modification method was used to prepare functional h-BN to improve its application potential in cement-based materials in this paper. The hydroxylated nano-boron nitride (h-BN-OH) was prepared by modified pristine h-BN with saturated sodium hydroxide (NaOH). The effects of h-BN-OH after ultrasonic dispersion for 10 min, 20 min, 30 min and 40 min on the setting time, fluidity, resistivity, mascroscopic strength and microscopic Young's modulus of hydration products of ordinary Portland cement were investigated. Fourier transform infrared spectroscopy (FTIR) test results showed that h-BN-OH had obvious hydroxyl infrared characteristic peaks. After adding h-BN-OH into cement paste, the initial and final setting time of cement paste was shortened 6.44–15.34% and 5.05–13.00%, respectively; the fluidity was reduced 9.86–22.79%, and the resistivity was increased 7.14–25.96%. Meanwhile, the compressive strength of cement paste and the microscopic Young's modulus of hydration products were significantly improved 10.82–40.85% and 9.90–31.01%, respectively. The main reasons were as follows: (1) The dispersion effect and stability of h-BN-OH in cement pore solution were better than that of pristine h-BN, and the hydroxyl group grafted on the h-BN-OH provided nucleation sites for the growth of calcium-silicate hydrate (C–S–H) gel. (2) The hydroxyl groups grafted on the h-BN-OH can absorb Ca 2+ , resulting the polymerization degree ( n c ) and medium chain length (MCL) of C–S–H gel increased. The formation of C–S–H gel network structure was accelerated by the increasing proportion of Q 3 . (3) The pore structure of cement hydration products was significantly optimized.

Combined effect of NaAlO2 and NaOH on the early age hydration of Portland cement with a high concentration of borate solution

Hydration kinetics and microstructure development of normal and NaAlO 2 ‐activated Al‐doped β‐C 2 S pastes

Effect of Alkali Content in Cement on Its Hydration Kinetics and Mechanical Properties

Effect of Borate Concentration on Solidification of Radioactive Wastes by Different Cements

Insights into the effect mechanism of nano LiAl-LDHs on the early hydration of sulphoaluminate cement-based materials

Effect of borax on the hydration and setting of magnesium phosphate cements

Chloride binding behaviors and early age hydration of tricalcium aluminate in chloride-containing solutions

Effects of Bauxite Tailings and Sodium Silicate on Mechanical Properties and Hydration Mechanism of Magnesium Phosphate Cement

Effects of Boric Acid on the Properties of Magnesium Oxysulfate Cement

Study on the hydration process and borax retarding mechanism of the magnesium ammonium phosphate cement-based coating system

Investigation on the Unusual Hydration and Hardening Process of a Portland Cement with Low Alkali Sulfate Content

Role of the structure of synthetic Al(OH)3 on the properties of sulfoaluminate cement-based materials

Effect and mechanism analysis of hydroxylated nano-boron nitride on workability and multi-scale mechanical properties of cement paste

Influence mechanism of retarders on the hydration of modified phosphoaluminate cement

Effect of blended inorganic salts containing negative hydration ions on hydration and properties of alkali-activated slag cement

Synthesis and Investigation of the Hydration Degree of CA2 Phase Modified with Boron and Fluorine Compounds

The Effect of Alcohol Compound on the Solidification of Magnesium Oxysulfate Cement-Boron Mud Blends

Effect of environmental pH values on phase composition and microstructure of Portland cement paste under sulfate attack

Effect of Gypsum on the Early Hydration of Cubic and Na-Doped Orthorhombic Tricalcium Aluminate

Effect of organic alkali on hydration of GGBS-FA blended cementitious material activated by sodium carbonate

Early Hydration and Viscoelastic Properties of Tricalcium Aluminate Pastes Influenced by Soluble Sodium Salts