Abstract:This study investigates how different sodium silicate SiO2/Na2O MS ratios (0.75, 0.9, and 1.2) affect the hydration behavior of amorphous wollastonitic hydraulic (AWH) binders containing various amounts of Al2O3 content (4, 7, 10, and 12%wt). The effects of and interaction between the MS ratio of the activator and the Al2O3 content of the sample on the hydration reaction and paste performance were investigated. The reaction was followed by calorimetry, and the pastes' compressive strength performances were tested at different curing times (2, 7, and 28 days). The hydrated pastes were characterized by FTIR, thermogravimetry analysis, and X-ray diffraction. The calorimetric results show that a higher Al2O3 cContent and a higher MS ratio result in a longer induction period. In terms of paste performance, an increase of the Al2O3 coupled with an activation with a 1.2 MS ratio results in a lower compressive strength after 28 days of hydration; the results range from 76 to 52 MPa. A decrease of the MS ratio to 0.9 allowed the obtention of a narrower range of results, from 76 to 69 MPa. Even though a decrease of the MS ratio to 0.75 led to higher hydration kinetics and high compressive strength results at early ages, at 28 days of curing, a decrease in compressive strength was observed. This may be a consequence of the fast kinetic of the mixture, since the rapid growth of hydration products may inhibit the dissolution at later ages and increase the porosity of the paste. Moreover, the high Al intake in the hydration product, facilitated by the high sodium content of the activator, promotes the formation of a higher number of calcium aluminate silicate hydrate structures (C-A-S-H) to the detriment of calcium silicate hydrate structures (C-S-H), decreasing the compressive strength of the samples. The TGA results indicate that the samples hydrated with the MS075 solution resulted in a higher number of hydrated products at early ages, while the samples hydrated with the MS09 and MS1.2 solutions exhibit a steady increase with curing time. Hence, an equilibrium in the hydration kinetic promoted by Si saturation-undersaturation appears to be fundamental in this system, which is influenced by both the MS ratio and the Al(OH)4- content in solution. The results of this study suggest that for this type of binder, optimal performance can be achieved by decreasing the MS ratio to 0.9. This composition allows for a controlled kinetic and overall higher compressive strength results in pastes produced with this AWH precursor.

Hydration kinetics and microstructure development of normal and NaAlO 2 ‐activated Al‐doped β‐C 2 S pastes

Hydration Characteristics of Tricalcium Aluminate in the Presence of Nano-Silica

Effect and mechanism of nano-Ca 10 (PO 4 ) 6 (OH) 2 additive on compressive strength of calcium aluminate cement at high temperature

Influence of Sodium Aluminate on Cement Hydration and Concrete Properties

Investigations of the Influence of Nano-Admixtures on Early Hydration and Selected Properties of Calcium Aluminate Cement Paste

Early Hydration and Viscoelastic Properties of Tricalcium Aluminate Pastes Influenced by Soluble Sodium Salts

Hydration kinetics of C3A: effect of lithium, copper and sulfur-based mineralizers

Insights into the effect mechanism of nano LiAl-LDHs on the early hydration of sulphoaluminate cement-based materials

Mitigating the Drying Shrinkage and Autogenous Shrinkage of Alkali-Activated Slag by NaAlO2

A study on the hydration of calcium aluminate cement pastes containing silica fume using non-contact electrical resistivity measurement

Development of a Novel Double-Sulfate Composite Early Strength Agent to Improve the Hydration Hardening Properties of Portland Cement Paste

Effect of two different crystal forms of alumina on hydration properties and mechanical properties of steel slag−cement composite cementitious materials

Hydration Properties of Alkali-Activated Quick Cooled Copper Slag and Slow Cooled Copper Slag

Examination of sulfate resistance of nano-alumina added ordinary Portland cement paste, focusing on the two different crystallinity of nano-aluminas

Combined effect of NaAlO2 and NaOH on the early age hydration of Portland cement with a high concentration of borate solution

Characteristics of CSH under carbonation and its effects on the hydration and microstructure of cement paste

Classical and new insights into the methodology for characterizing the hydration of calcium aluminate cements

Hydration Characteristics of Calcium Sulfoaluminate-Fly Ash Mixed with Different Alkalies

Toward performance improvement of supersulfated cement by nano silica: Asynchronous regulation on the hydration kinetics of silicate and aluminate

Microstructural evolution and degradation mechanisms of tricalcium silicate and tricalcium aluminate composite pastes under sulfate exposure

Influence of Silica Modulus on the Activation of Amorphous Wollastonitic Hydraulic Binders with Different Alumina Content: Study of Hydration Reaction and Paste Performance