Abstract:Bayer red mud (RM) occupies a large amount of land, which excessive Na+ seriously damages groundwater resources. In this research, a RM based cementitious material (RMC) composed of RM and ordinary Portland cement (OPC) was developed. It is interesting to find that a binary reaction consisting of cement hydration and geopolymer reaction in RMC. The mechanical and Na+ consolidation rate of RMC were improved by the synergistic effect of binary reaction. The results indicated that the compressive strength of RMC is the highest and reaches 32.5R OPC when the mass ratio of CaO/(SiO2+Al2O3) is 1.37, and the Na+ leaching concentration is environmentally acceptable. The 7 days compressive strength of RM-based cementitious material No.2 (RMC2) can reach 93.80% of that of 28 days. As the predominant hydration products, cement hydration product (Ca5(SiO4)2(OH)2) and geopolymer (CaAl2Si2O8·2H2O and Na3Al3Si3O12·2H2O) were principally responsible for the strength development of RMC2 at 7 days. The optimal densification microstructure and [SiO4] polymerization structure was presented in RMC2. The supreme Na+ consolidation rate was 99.23% in RMC2 due to the cooperation of physical fixation and [Si(Al)O4] charge balance principle. This paper provides a fresh theoretical guidance for the utilization of RM and its Na+ in building materials.

Effects of alkali and alkaline-earth oxides on preparation of red mud based ultra-lightweight ceramsite

Effects of Red Mud on Workability and Mechanical Properties of Autoclaved Aerated Concrete (AAC)

Preparation of ultra-lightweight ceramsite from red mud and immobilization of hazardous elements

Strengthening Mechanism of Red Mud with Calcium Oxide

Process optimization for the synthesis of ceramsites in terms of mechanical strength and phosphate adsorption capacity

Novel Glass Ceramic Foams Materials Based on Red Mud

Effect of Red Mud on Mechanical Properties of Loess–Containing Aluminosilicate Based Cementitious Materials

Toughening Mechanism of CaAl12O19 in Red Mud–Al2O3 Composite Ceramics

Numerical Simulations of the Impact of CaO/Al2O3 on the Structure and Crystallization Behavior of Red Mud

Construction Ceramsite from Low-silicon Red Mud: Design, Preparation, and Sintering Mechanism Analysis

Preparation of ultra-lightweight ceramsite from waste materials: Using phosphate tailings as pore-forming agent

Mechanism of Na2CO3 on Early Properties of Red Mud-Based Alkali-Activated Cementitious Materials

Preparation of ceramsite from low-silicon red mud (LSRM): Effects of Si–Al ratio and sintering temperature

Preparation and properties of high-strength lightweight aggregate ceramsite from nepheline tailings

Effect of pore structure characteristics on the properties of red mud-based alkali-activated cementitious materials

Material properties and environmental implications of red mud solidified with blast-furnace slag, silica fume, and sodium hydroxide

Utilization of Red Mud with High Radiation for Preparation of Autoclaved Aerated Concrete (AAC): Performances and Microstructural Analysis

Study on the effect of sodium removal from citric acid pretreated red mud on the physical properties of red mud

Binary reaction behaviors of red mud based cementitious material:Hydration characteristics and Na+ utilization

Alkali-activated red mud in stabilizing marine dredged clay with low amount of cement

Improving foamed mixture lightweight soil containing red mud properties by utilizing nano-SiO2