Evaluation of fracture properties of annealed Fe–Si–B–Cr amorphous alloys using micro-tensile tests and blanking machinability

Chieko Kuji,Masayoshi Mizutani,Keita Shimada,Ken Suzuki,Hideo Miura,Tsunemoto Kuriyagawa

DOI: https://doi.org/10.1016/j.msea.2022.143483

2022-07-19

Abstract:In this study, the change in the strength of B-rich Fe-based amorphous alloy was investigated as a function of its microstructure controlled by the annealing at temperatures from 713 to 873 K. The strength was measured by using a micro-tensile test in a focused ion beam apparatus, and its machinability was tested by a blanking test. It was found that the static strength and machinability of the alloy varied drastically depending on its microtexture. In the micro-tensile test, the as-received sample exhibited ductile fracture with a tensile strength of about 1200 MPa, concurring with the bulk material. During the annealing up to 773 K, fine Fe3B crystals stared to precipitate sparsely in the matrix, and α-Fe crystals grew around Fe3B the crystals. Due to this microstructural change, the tensile strength dropped down to about 300 MPa, the fracture mode changed from ductile to brittle, and the toughness of the alloy decreased significantly. However, when the annealing temperature exceeded 773 K, the microtexture changed to clear polycrystalline, and thus, large plastic deformation reappeared, and the tensile strength returned to about 900 MPa. The blanking test revealed that the annealing reduced the blanking resistance significantly, in particular, in the sample annealed at 763 K. High-quality machining traces without burrs and shear droops were obtained from this sample. From the viewpoint of machinability, it was concluded that the microstructure with the fine precipitates dispersed in the amorphous matrix was most appropriate for this amorphous alloy.