Abstract:Early-age cracking in mass concrete structures resulting from thermal stress is a well-documented phenomenon that impacts their functionality, durability, and integrity. The primary cause of these cracks is the uneven temperature rise within the structure due to the exothermic nature of cement hydration. Assessing the likelihood of cracking involves comparing the tensile strength or strain capacity of the concrete with the stresses or strains experienced by the structure. Challenges in evaluating the risk of thermal cracking in mass concrete structures stem from various material and technological factors that influence the magnitude and progression of hydration heat-induced temperature and thermal stress. These complexities can be addressed through numerical analysis, particularly finite element analysis (FEA), which offers comprehensive modeling of early-age effects by considering all pertinent material and technological variables. However, employing FEA poses challenges such as the requirement for numerous input parameters, which may be challenging to define, and the need for specialized software not commonly available to structural engineers. Consequently, the necessity for such advanced modeling, which demands significant time investment, may not always be warranted and should be initially assessed through simpler methods. This is primarily because the definition of massive structures-those susceptible to adverse effects such as cracking due to temperature rise from hydration heat-is not precise. To address these challenges, the authors propose a three-step method for evaluating structures in this regard. The first step involves a simplified method for the classification of massive structures. The second step entails estimating hardening temperatures and levels of thermal stress using straightforward analytical techniques. The third step, reserved for structures identified as having a potential risk of early thermal cracks, involves numerical modeling. The outlined procedure is illustrated with an example application, demonstrating its practicality in analyzing a massive concrete wall constructed on the foundation.

Early‐age cracking due to restraint: Laboratory and field investigations on the predictive capacity of the simplified method in Annex D of the future EC2

INCORPORATING PRE-EXISTING CRACKS IN STRUCTURAL ASSESSMENT OF RC STRUCTURES

Uniaxial Concrete Tension Damage Evolution Using Acoustic Emission Monitoring

Multi-Step Procedure for Predicting Early-Age Thermal Cracking Risk in Mass Concrete Structures

Practical insights on standardised models for estimation of crack width due to imposed strains in edge-restrained reinforced concrete elements

Early Age Properties and Cracking Control of Concrete

Cracking assessment via a simplified approach – case of the gusset of the VeRCoRs nuclear power plant mock-up

Application of Equivalent Age Method to Concrete Thermal Cracking Control at Early Ages

Analytical Prediction and Experimental Research on Shrinkage Cracking of Restrained Early-Age Concrete

Prediction of residual stress due to early age behaviour of massive concrete structures: on site experiments and macroscopic modelling

YOUNG CONCRETE THERMAL CRACKING CONTROL BASED ON EQUIVALENT AGE METHOD

Analyzing of Cracking Risk of Early-age Concrete Structure

THEORETICAL INVESTIGATION TO CRACKING PREDICTION OF EARLY-AGE CONCRETE

Insight into Thermal Stress Distribution and Required Reinforcement Reducing Early-Age Cracking in Mass Foundation Slabs

Estimation of Thermal Stresses in the Field Test under the Restraint Method

Assessment and mitigation of early-age cracking for on-site concrete structures by a combined scheme using Temperature Stress Testing Machine (TSTM) and long-span restraining frame

Numerical simulation of cracking of early-age concrete three-point beams

Factors affecting the thermo-chemo-mechanical behaviour of massive concrete structures at early-age

EXPERIMENTAL AND NUMERICAL ANALYSIS OF EARLY-AGE STRESS IN CONCRETE DIAPHRAGM WALL OF UNDERGROUND STRUCTURES

Experimentally informed modeling of the early‐age stress evolution in cementitious materials using exponential conversion from creep to relaxation

Research On The Crack Risk Of Early-Age Concrete Under The Temperature Stress Test Machine