Abstract:The external ambient temperature plays a crucial role in influencing the hydration process of cemented paste backfill (CPB), causing notable variations in overall structure and physicalmechanical properties. To precisely analyze mechanical properties under different curing temperatures, a uniaxial compression strength (UCS) experiment was conducted. A real-time data acquisition system was established to monitor temperature, volumetric water content, and resistivity. Hydration heat measurement and low-field nuclear magnetic resonance (NMR) experiments were performed to analyze the hydration mechanism and the correlation between mechanical properties and thermal effects during the consolidation period. The study revealed that the relationship between UCS, elastic modulus, and curing temperature can be quantitatively characterized using polynomial functions. The mechanical parameters reach their peak values at a curing temperature of 40 degree celsius. However, exceeding 40 C leads to excessively rapid hydration rates, causing a decrease in hydration degree, and extremely high hydration rates result in reduced microstructure compactness. Under different curing temperature conditions, CPB exhibits substantial temperature effects in terms of volumetric water content, electrical resistivity, hydration heat, and NMR data, effectively characterizing the hydration mechanism. The hydration reaction unfolds through stages: initial induction, accelerated development, decelerated development, stable development, and hardening formation. As the curing temperature rises, the completion times of each stage exhibit a significant exponentially decreasing trend. Moreover, the application of the GA-BP neural network algorithm has unveiled inherent patterns between the monitoring results of CPB's hydration process and its macroscopic strength. Computed results show that the relative errors in predicting strength at various curing temperatures are all less than 0.1 %.

Characterizing the hydration process of cement based on synchronous thermal analysis method

The Early-Age Drying Shrinkage of Cement-Based Materials with the Same Workability after Temperature Compensation

Micro Expressions of Cement Hydration Kinetics

Model for Hydration Heat of Cement in Concrete and Its Application

Experimental Study on Temperature Characterization During Cement Grouting Reinforcement

Early Hydration Properties and Reaction Kinetics of Multi-Composite Cement Pastes with Supplementary Cementitious Materials (Scms)

The Early Hydration of OPC Investigated by In-Situ XRD, Heat Flow Calorimetry, Pore Water Analysis and 1H NMR: Learning about Adsorbed Ions from a Complete Mass Balance Approach

Concrete Thermal Cracking Analysis with Cement Hydration Model and Equivalent Age Method

Isothermal Calorimetry Tests and Modeling of Cement Hydration Parameters

Hydration Mechanism and Mechanical-Thermal Correlation of Cemented Paste Backfill under Different Curing Temperatures

Application of X-Ray Micro-CT for Quantifying Degree of Hydration of Slag-Blended Cement Paste

Programmatic Data Analysis for Quantitative Isothermal Heat Flow Calorimetry of Cementitious Materials

Calorimetric Study of Ternary Binder of Calcium Aluminate Cement, Portland-limestone Cement and FGD Gypsum

Utilizing optical spectroscopy and 2',7'-difluorofluorescein to characterize the early stages of cement hydration

Quantifying early age hydration and micro-structure evolution of fast setting binder using 1 H NMR

Study on optimization of hydration process of blended cement

Experimental study of pure Class G cement hydration up to 150oC and 50MPa

Recent Development on Understanding Cement Hydration Mechanism and Effects of Chemical Admixtures on Cement Hydration

Advances in understanding hydration of Portland cement

Calorimetric Study of Calcium Aluminate Cement Blended with Flue Gas Desulfurization Gypsum

Modeling the hydration, viscosity and ultrasonic property evolution of class G cement up to 90 °C and 200 MPa by a scale factor method