Abstract:Manufacturing CuCrZr alloy parts with high strength and high surface quality by selective laser melting (SLM) is a challenging task. This study investigates the microstructure, mechanical properties and machinability of SLM processed and heat-treated CuCrZr alloy through tensile test, compression test and ultra-precision machining. The microstructure analysis shows that the grain morphology and orientation are highly related to the laser track and building direction. Grain epitaxial growth is found on both horizontal (XY) and vertical (XZ) planes, which bends at the boundary of the molten track/pool. After heat treatment, molten track boundaries disappear and the slender and bent grains on the XY plane are replaced by polygonal square grains, but the large epitaxial grains on the XZ plane still remained. X-ray diffraction results indicate that the as-built sample contains α-Cu, Cr and CuxZry phases and building direction has an influence on the crystallographic orientation distribution. As-built (AB) CuCrZr alloy shows a comparable yield strength (218.0 MPa) with solution + ageing-treated (SAT) (231.3 MPa), which is much higher than that of the solution-treated (ST) counterpart (131.0 MPa). Although the ultimate tensile strength of the AB sample is lower than that of the SAT sample, its elongation at break (46.5%) is much higher than the latter (19.1%). The compressive strength of the AB sample is slightly lower than the SAT sample but higher than the ST sample. At low cutting speed, the ST sample shows a higher cutting force. High cutting speed will lead to the increase of cutting force of the AB and SAT samples but has a much lower effect on the ST sample. The XZ plane of the AB sample shows better machined surface quality. SAT sample has the highest material recovery during cutting and its chip will change from spiral to arc shape with the increase of cutting speed.

Influence of Selected Factors of Vibratory Work Hardening Machining on the Properties of CuZn30 Brass

Investigation of fracture mechanical properties of a brass alloy with microstructural variations

Correlation between microstructural deformation mechanisms and acoustic parameters on a cold-rolled Cu30Zn brass

The Effect of Selected Parameters of Vibro-Abrasive Processing on the Surface Quality of Products Made of 6082 Aluminium Alloy

A micromechanical study of heat treatment induced hardening in α-brass

Influence of Water Jet Peening on Surface Strengthening of Brass

The Influence of Vibro-Assisted Abrasive Processing on the Surface Roughness and Sub-Surface Microstructure of Inconel 939 Specimen Made by LPBF

Tribological Performance of Multiscale Micro-Textured H62 Brass Surface Fabricated by Micro-Milling and Wet Micro-Blasting

Fabrication of Copper of Harmonic Structure: Mechanical Property-Based Optimization of the Milling Parameters and Fracture Mechanism

Influence of the sintering method on microstructure and microhardness of AlCuNiSnZn-based high-entropy brasses and bronzes obtained by powder metallurgy

Chemical Composition of New Copper Alloys for Machining and Its Effect on Their Susceptibility to Corrosion Cracking

Contribution of Process Annealing on the Development of Microstructure and Texture of Cu-30Zn Brass

Investigations on the effect of wire EDM process parameters on surface integrity of HSLA: a multi-performance characteristics optimization

Study on surface texture and corrosion resistance of ultrasonic vibration-assisted micromilling Inconel718

Experimental Analysis Of The Effect Of Mechanical Properties And Microstructure On Tool Vibration And Surface Quality In Dry Turning Of Hardened Aisi 4340 Steels

Influence of cutting speed on fretting wear properties of UVAM-processed NAB alloy

Additively manufactured CuCrZr alloy: Microstructure, mechanical properties and machinability

Influence of grain size and grain boundaries on the thermal and mechanical behavior of 70/30 brass under electrically-assisted deformation

Influence of surface burnishing process with single strain path and reciprocating strain path on copper wear behavior

Research On Surface Strengthening Induced By Ultrasonic Punching To Improve Mechanical Properties And Corrosion Resistance For Shaft Parts

The Influence of Impac-Oscilation Loading on the Hardness of Surface Layers of D16ChATW Aluminum Alloy