Abstract:The relationship between acoustic parameters and the microstructure of a Cu30Zn brass plate subjected to plastic deformation was evaluated. The plate, previously annealed at 550 °C for 30 minutes, was cold rolled to reductions in the 10-70\% range. Using the pulse-echo method, linear ultrasonic measurements were performed on each of the nine specimens, corresponding to the nine different reductions, recording the wave times of flight of longitudinal wave along the thickness axis. Subsequently, acoustic measurements were performed to determine the nonlinear parameter ($\beta$) through the second harmonic generation. X-ray diffraction analysis revealed a steady increase and subsequent saturation of deformation twins at 40\% thickness reduction. At higher deformations, the microstructure revealed the generation and proliferation of shear bands, which coincided with a decrease in the twinning structure and an increase in dislocation density rate. Longitudinal wave velocity exhibited a 0.9\% decrease at 20\% deformation, followed by a continuous increase of 2\% beyond this point. These results can be rationalized as a competition between a proliferation of dislocations, which tends to decrease the linear sound velocity, and a decrease in average grain size, which tends to increase it. These variations are in agreement with the values obtained with XRD, Vickers hardness and metallography measurements. The nonlinear parameter $\beta$ shows a significant maximum, at the factor of 8 level, at 40\% deformation. This maximum correlates well with a similar maximum, at a factor of ten level and also at 40\% deformation, of the twinning fault probability.

What problem does this paper attempt to address?

This paper aims to explore the microstructural changes in cold-rolled Cu30Zn brass under different degrees of deformation and their impact on acoustic parameters. Specifically, the study evaluates the microstructural changes during the plastic deformation process through linear ultrasonic measurements and nonlinear ultrasonic parameter analysis. The main focus includes: 1. **Microstructural Changes**: - The study found that with increasing deformation, shear bands and twinning appeared within the material, and twinning reached saturation at 40% deformation. - As deformation further increased, shear bands began to form and multiply. 2. **Linear Ultrasonic Measurements**: - Linear ultrasonic measurements were conducted on nine samples with different degrees of deformation, recording the propagation time of longitudinal waves along the thickness direction. - It was found that at 20% deformation, the longitudinal wave velocity decreased by 0.9%, and then gradually increased with further deformation, eventually increasing by 2% compared to the initial state. 3. **Nonlinear Ultrasonic Parameters**: - The nonlinear parameter 𝛽∗ was determined using the second harmonic generation (SHG) method. The results showed that at 40% deformation, the 𝛽∗ value significantly increased, reaching 8 times the level of the initial state. 4. **X-ray Diffraction Analysis**: - X-ray diffraction analysis revealed that with increasing deformation, the number of twins first increased and then tended to saturate, and shear bands appeared at higher degrees of deformation. - Microstrain increased with deformation, while grain size rapidly decreased initially and then slowly reduced. In summary, this study aims to understand the microstructural evolution mechanism of cold-rolled Cu30Zn brass during the plastic deformation process through changes in acoustic parameters.

Correlation between microstructural deformation mechanisms and acoustic parameters on a cold-rolled Cu30Zn brass

Tensile Deformation and Fracture Behaviours of Cold Rolled Cu-3wt.%Ag-0.5wt.%Zr Thin Sheets with Different Annealed Microstructures

Investigation of fracture mechanical properties of a brass alloy with microstructural variations

Effect of Annealing on the Microstructure, Texture and Tensile Deformation Properties of Cu–3 Wt%ag–0.5 Wt%zr Thin Sheets Rolled at Room and Cryogenic Temperature

Ultrasonic vibration-induced severe plastic deformation of Cu foils: effects of elastic-plastic stress wave bounce, acoustic softening, and size effect

Ultrasonic Assessment of the Influence of Cold Rolling and Recrystallization Annealing on the Elastic Constants in a TWIP Steel

Contribution of Dislocation Evolution to Acoustic Nonlinearity in Plastically Damaged Materials

Shear band mediated microstructure in an accumulative roll bonded α-brass alloy during strain path changes and annealing

Influence of Microstructure and Strain Hardening Rate on Acoustic Nonlinearity Parameter in Stainless Steel 316L during Tensile Loading

Molecular dynamics study of acoustic softening effect in ultrasonic vibration assisted tension of monocrystalline/polycrystalline coppers

Revealing the Microstructure Evolution Mechanism and Mechanical Responses of a Novel Al–Zn–Mg–Cu Alloy by Hot Deformation Process

Effect of cryogenic rolling on the microstructure and texture of CuCrZr alloy

Effects of Cold Rolling Reduction Rate on the Microstructure and Properties of Cu-1.16Ni-0.36Cr Alloy after Thermo-Mechanical Treatment

Influence of the Metal Structure and Plastic Deformation on the Nonlinear Acoustic Parameter

Deformation induced phase transition in brass under shock compression

Influence of Selected Factors of Vibratory Work Hardening Machining on the Properties of CuZn30 Brass

Effect of cryogenic rolling and multistage thermo-mechanical treatment on the microstructure and properties of the Cu-0.4Cr-0.39Zn-0.1Mg-0.07Zr alloy

Microstructural evolution and mechanical properties of pure zinc subjected to extrusion and caliber rolling

A micromechanical study of heat treatment induced hardening in α-brass

Microstructural evolution and strengthening mechanisms in cold-rolled Cu–Ag alloys

Influence of grain size and grain boundaries on the thermal and mechanical behavior of 70/30 brass under electrically-assisted deformation