Abstract:<p>In this work, the microstructural evolution and strengthening mechanisms of pure copper and Cu–Ag alloys subjected to cold rolling were experimentally investigated. Significant strain strengthening occurred during cold rolling, with steady-state strengths of 424, 666, and 686 MPa achieved upon large-strain cold rolling in pure copper, Cu–10Ag, and Cu–15Ag, respectively. Microstructural examination was performed to quantitatively determine the strengthening contributions of the grain boundaries, dislocations, Ag dispersoids, and solute atoms. Dislocation strengthening and boundary strengthening were shown to be the dominant strengthening mechanisms in the cold-rolled Cu–Ag alloys at steady state, accounting for >80% of the strengthening. In addition, Ag addition increased the limiting concentration of dislocations and subgrain boundaries in the Cu solid solution, resulting in higher steady-state strength of the cold-rolled Cu–Ag alloys relative to that of pure copper. The high Ag concentration also led to a larger volume fraction of the high-strength eutectic colony in Cu–15Ag, resulting in higher strength than that of Cu–10Ag.</p>

What problem does this paper attempt to address?

The paper mainly explores the effects of cold rolling on the microstructural evolution and strengthening mechanisms of copper-silver (Cu–Ag) alloys. ### Research Background and Objectives - **Research Subjects**: Pure copper, copper alloy containing 10% silver (Cu–10Ag), and copper alloy containing 15% silver (Cu–15Ag). - **Research Objectives**: - Experimentally investigate the microstructural evolution and strengthening mechanisms of these materials during the cold rolling process. - Quantitatively analyze the contributions of solute atoms, dislocations, and phase sizes to the material strength. - Clarify how the addition of silver affects the solid solution strengthening, boundary strengthening, and dislocation strengthening of cold-rolled Cu–Ag alloys. ### Main Findings - **Significant Strain Hardening Phenomenon**: With the increase in cold rolling strain, the steady-state strengths of pure copper, Cu–10Ag, and Cu–15Ag reached 424 MPa, 666 MPa, and 686 MPa, respectively. - **Dominant Strengthening Mechanisms**: Dislocation strengthening and boundary strengthening are the main strengthening mechanisms in the steady state of cold-rolled Cu–Ag alloys, together contributing over 80% of the total strengthening effect. - **Role of Silver Element**: - Increased the maximum concentration of dislocations and subgrain boundaries in the copper matrix, thereby enhancing the steady-state strength of cold-rolled Cu–Ag alloys. - High concentration of silver led to an increased volume fraction of high-strength eutectic clusters in Cu–15Ag, further enhancing the material strength. ### Microstructural Analysis - **Eutectic Structure**: Cu–Ag alloys consist of a copper-rich phase and eutectic clusters, with the eutectic clusters mainly located at the grain boundaries of the copper-rich phase. - **Subgrain Refinement**: A large number of fine subgrains formed during the cold rolling process, which helps to improve the material strength. - **Dislocation Density**: With the increase in cold rolling strain, the dislocation density significantly increased and reached a stable value. ### Discussion on Strengthening Mechanisms - **Solid Solution Strengthening**: The lattice distortion caused by silver atoms dissolving in the copper matrix leads to a solid solution strengthening effect. - **Dispersion Strengthening**: The thin band-like structures formed by silver particles during cold rolling provide a slight strengthening effect. - **Dislocation Strengthening**: The high density of dislocations introduced by cold rolling is one of the main sources of strength improvement. - **Boundary Strengthening**: The presence of fine subgrains and the reduction in the thickness of eutectic clusters both contribute to enhancing the boundary strengthening effect of the material. In summary, this paper experimentally reveals the effects of cold rolling on the microstructure and strengthening mechanisms of Cu–Ag alloys and quantitatively analyzes the contributions of different factors to the material properties. The addition of silver not only enhances the material properties through solid solution strengthening but also promotes the formation of dislocations and subgrain boundaries, thereby improving the overall strength of the material.

Microstructural evolution and strengthening mechanisms in cold-rolled Cu–Ag alloys

Reforming Nanostructured CuAg Alloy to Improve Ductility and Electrical Conductivity

Microstructure evolution and properties of Cu–Ag microcomposites with different Ag content

Strengthening Effect of Ag Precipitates in Cu–Ag Alloys: A Quantitative Approach

Tensile strength and Young's modulus of Cu-Ag alloys in the evolution of microstructure into filamentary composites

Microstructural evolution and strength of copper during cold rolling to large strain

Effect of cold rolling on aging precipitation behavior and mechanical properties of Cu–15Ni–8Sn alloy

Relationships between mechanical strength and electrical conductivity for Cu–Ag filamentary microcomposites

Co-deformation in Cu–6 Wt.% Ag Nanocomposites

Effects of Cr and Zr additions on the microstructure and properties of Cu-6wt.% Ag alloys

Improvement of mechanical properties and thermal stability of Al–Cu–Mg–Ag alloy by warm rolling

Deformation of Fe and Ag Precipitates in Cu Matrix

Microstructure and properties of Cu-Ag alloy prepared by continuously directional solidification

Synergistic strengthening effects of precipitation and work hardening in cold-rolled Cu-0.4 wt%Cr alloy

Effect of cold rolling on microstructure and mechanical properties of a Cu–Zn–Sn–Ni–Co–Si alloy for interconnecting devices

Microstructure and properties of Cu–Ag, Cu–Ag–Cr and Cu–Ag–Cr–RE alloys

Effects of Cold Rolling Pre-Strain on Abnormal Grain Growth Behavior in Longitudinal Welds of 2196 Al-Cu-Li Profiles

Mechanical property enhancement and microstructure evolution of an Al-Cu-Li alloy via rolling at different temperatures

Achieving High Strength and High Conductivity of Cu-6 wt%Ag Sheets by Controlling the Aging Cooling Rate

Cold deformation behavior and microstructure evolution of biomedical Cu-containing L605 alloy

Effect of cold rolling deformation on the microstructure and mechanical properties of spray-formed Al–Zn–Mg–Cu alloy