Abstract:Pure copper is very soft, however, hardening the pure copper with most strengthening mechanisms leads to a significant reduction in electrical conductivity. Grain refinement is a better strengthening mechanism to maintain high enough electrical conductivity. Plastic deformation at room temperature followed by post-annealing is one of the best methods to achieve fine-grained metals and alloys. In this research, the high-temperature annealing behavior of cold-rolled electrolytic tough-pitch (ETP) copper sheets was studied. 90 % asymmetric cold rolling followed by high-temperature post-annealing at 673 K for 1, 2, 5, 10, 30, 60, and 120 min were applied on the copper. The microstructure was significantly changed with increasing annealing time from 1 to 2 min owing to full recrystallization. With increasing the annealing duration, the grain size is increased. The formation of equiaxed grains with a smaller size (∼9 μm) compared to the full-annealed (initial) sample (∼68 μm) is observed after the longest time of post-annealing (120 min) due to the pinning effect of Cu2O particles. The post-annealed copper sheets processed by asymmetric rolling (in this work) exhibited a more homogeneous microstructure through the thickness compared to the symmetric rolling due to more uniform stored strain energy. The results showed that the first deformed grains that undergo recrystallization during post-annealing are Goss-oriented grains. With an increase in the post-annealing time, the S and Copper components were eliminated and a strong Cube and P texture orientations were formed. Interestingly, after 1 min of post-annealing, the yield and tensile strength enhanced to 410.2 MPa and 418.6 MPa owing to the annealing hardening phenomenon. The hardness and strength reached a constant value after the post-annealing for 10 min and above. With increasing the post-annealing duration, the central area of fracture surfaces (consisting of ductile dimples) became larger and the outer region (consisting of flat surfaces and shear dimples) became smaller, showing a shift towards perfect ductile fracture. With the increase of post-annealing time from 1 min to 120 min, the electrical conductivity was increased from 77.6 to 97.5 %IACS. The presence of the Cube texture increased the electron mobility compared to the P orientation, by reducing the mean distance that they can travel without scatter. From the obtained results, it can be concluded that the asymmetric cold rolling followed by high-temperature post-annealing is capable of strength improvement and maintaining electrical conductivity in copper.

Contribution of Process Annealing on the Development of Microstructure and Texture of Cu-30Zn Brass

A micromechanical study of heat treatment induced hardening in α-brass

Shear band mediated microstructure in an accumulative roll bonded α-brass alloy during strain path changes and annealing

Microstructure and Texture Evolution in Cold-Rolled and Annealed Oxygen-Free Copper Sheets

Effect of annealing processes on microstructure, mechanical properties and conductivity of Cu-12%Ag alloy composite-reinforced by fibers

New insight of texture and microstructure evolution, and the connections between with tensile performance in as-annealed Al-Cu-Mg-Zr sheet

Effect of Annealing Process on the Microstructure and Texture of Cold-Rolled High-Purity Al-0.5%Cu Plates

Investigation of fracture mechanical properties of a brass alloy with microstructural variations

The Dependence of Final Microstructure, Texture Evolution and Mechanical Properties of Al–Mg–Si–Cu Alloy Sheets on the Intermediate Annealing

Effect of cross cold rolling and annealing on microstructure and texture in pure nickel

High-temperature annealing behavior of cold-rolled electrolytic tough-pitch copper

Microstructure and Bending Properties of Cu-Cr-Zr Alloy Subjected to Heat Treatment and Rolling

Effect of annealing treatment on texture evolution, microstructure and mechanical properties of an extruded Mg-Gd-Zn-Zr alloy

Microstructure Evolution and Cooperative Strengthening Mechanism of Copper–Aluminum Bimetal Continuous Equal Channel Angular Pressing-Annealing Process

Microstructure and Texture Evolution in Thermomechanically Processed FCC Metals and Alloys: a Review

Microstructure and properties of Al-4.8Cu-0.45Mn-0.19Cd-0.18Ti-0.17Zr-0.14V aluminum alloy extrusion bar

Effects of Different Modes of Hot Cross-Rolling in 7010 Aluminum Alloy: Part I. Evolution of Microstructure and Texture

Effect of Annealing on the Microstructure, Texture, and Properties of Cold-Rolled Ti50Ni47Fe3 Shape Memory Alloy Sheets

Microstructure and Mechanical Properties of Ultrafine-Grained Copper by Accumulative Roll Bonding and Subsequent Annealing

Influence of annealing conditions on the mechanical and microstructural behavior of electroplated Cu-TSV

Developing Alternative Texture in a 90Cu-10Zn α-Brass Alloy via Route Changes in Accumulative Roll Bonding Process