Abstract:The interface morphology of the bonding layer has a considerable effect on the damage and failure of sandwich-structured thermal barrier coatings. This work investigated the comprehensive effects of a grooved texture produced using laser ablation on the local surface strain, interfacial stress and strain, and crack behavior of the bonding layer in a thermal barrier coating system. The distribution and evolution of the local surface strain was obtained using the digital image correlation method. The interfacial stress, and the strain between the ceramic and bonding layers, were determined through a simulation of the plane-strain model, and the morphology and propagation of cracks were observed in thermal barrier coatings under an external tensile load. The results indicated that the local surface strain of the thermal barrier coating increased with the texturization of the bonding layer, whereas the fluctuation decreased. There were two inflection points in the local surface strain–time curves, corresponding to the initiation of surface cracks and that of interfacial transverse cracks. The surface cracks were initiated earlier than those without the texturization of the bonding layer. However, the behavior of the interfacial cracks was more complicated. If the roughness of the texture, defined as Rc, was small, the surface cracks propagated vertically to the interface between the ceramic and bonding layers, and turned into transverse cracks, leading to a separation of the ceramic layer. If Rc was greater than 22 μm, the surface cracks went further down to the interface between the bonding layer and substrate, and propagated horizontally, resulting in the separation of both the ceramic and bonding layers. Meanwhile, interfacial cracking and separation were deferred. A large roughness resulted in good cohesion between the ceramic and bonding layers, and a high stiffness for the coating, which improved the damage resistance and extended the life of the coating.

Discrete element modeling of effect of interfacial roughness and pre-crack on crack propagation in thermal barrier coatings

A Simulation Study on the Crack Propagation Behavior of Nanostructured Thermal Barrier Coatings with Tailored Microstructure

A Diffusion-Coupled Cohesive Element Model for Cracking Analysis of Thermal Barrier Coatings

On crack evolution with texturization of bonding layer in thermal barrier coating

Influences of Interface Properties and Coating Thickness on Fracture Behaviors of Coating/substrate Systems

Simulation of Residual Stresses and Their Effects on Thermal Barrier Coating Systems Using Finite Element Method

Effect of the interface morphology and initial nanocrack on the fracture property of a ceramic reinforced plasma-sprayed coating

Computational analysis of thin coating layer failure using a cohesive model and gradient plasticity

Effect of interface on the thermal conductivity of thermal barrier coatings: A numerical simulation study

Finite Element Analysis of Interface Undulation and Interface Delamination in the MCrAlY Coating System Under Thermal Cycling: Considering Oxide Thickness and Top-Coat Effects

Influence of crack and pore structure characteristics on the thermal protective performance of thermal barrier coatings based on LBM

Internal-interfacial cracking interaction: Combined phase-field and discontinuous Galerkin/cohesive zone modeling

PHASE FIELD SIMULATION FOR HIGH-TEMPERATURE OXIDATION BEHAVIOR OF THERMAL BARRIER COATINGS UNDER SHOT PEENING

Numerical study of thermomechanical delamination mechanisms in segmented high-temperature coatings

Microcrack Morphology in the Thermal Insulation Performance of 8YSZ Thermal Barrier Coatings: A Mesoscale Numerical Study

Crack nucleation and propagation simulation in brittle two-phase perforated/particulate composites by a phase field model

Failure Characterization of Solid Structures Based on an Equivalence of Cohesive Zone Model

Effect of Interface Curvature on Local Growth Behavior and Stress of Thermal Barrier Coatings

Effect of the thermally grown oxide and interfacial roughness on stress distribution in environmental barrier coatings

Modeling 3D TGO dynamic growth and stresses and the resulting modes of buckling failure in thermal barrier coatings

Effect of Binder Coatings on the Fracture Behavior of Polymer–Crystal Composite Particles Using the Discrete Element Method