Electrical and Ferroelectric Properties of Strontium Doped Lead-Free BCZT Ceramics
Ritesh Verma,Muskan Saini,Ankush Chauhan,Rohit Jasrotia,Rahul Kalia,Leena Bhardwaj,Atul Thakur
DOI: https://doi.org/10.1149/2162-8777/ad5589
IF: 2.2
2024-06-20
ECS Journal of Solid State Science and Technology
Abstract:Herein, we synthesized Ba 0.9-x Ca 0.1 Sr x Ti 0.8 Zr 0.2 O 3 (x = 0.05, 0.1, 0.15, 0.2) ceramic samples by employing a solid-state reaction technique. The variation of dielectric constant is studied concerning temperature in the range 1 kHz to 1 MHz frequency. Variation of dielectric constant ( ε r ) with temperature reveals that charge carrier dispersion pushes the transition temperature towards higher frequency. Impedance analysis reveals that the maximum value of the imaginary part of impedance i.e., Z ′′ maxima, increases in all samples except for x = 0.05, which shows the opposite behaviour. This behaviour is due to the calcium (Ca 2+ ) substitution at the titanium (Ti 4+ )-site at low doping concentration of Sr 2+ ions. Nyquist plots show the presence of a single semi-circular arc, indicating the contribution of resistance and capacitance through grain boundary. PE hysteresis loops reveal that the values of saturation polarization ( P s ) decrease with increasing Sr-doping, from 10.989 μC cm −2 to 6.586 μC cm −2 , whereas the remnant polarization ( P r ) shows variable values with increasing Sr-doping.
materials science, multidisciplinary,physics, applied