Composition and property correlation of Nd3+ ion doped (Na0·5Bi0.5) TiO3 Lead-free ceramics

Jyothi Neeli,Nitchal Kiran Jaladi,Vijaya Lakshmi Garlapati

DOI: https://doi.org/10.1016/j.jssc.2023.124430

IF: 3.3

2024-01-01

Journal of Solid State Chemistry

Abstract:Physicochemical, optical, magnetic, and mechanical properties of ceramic compositions of Na0·5[Bi1-xNdx]0.5TiO3 (NBNdxT) (x = 0.0, 0.1, 0.3, and 0.5) were obtained from the solid-state reaction method. X-ray diffraction (XRD) confirmed the primary rhombohedral phase of perovskite belonging to the space group R3c. SEM analysis revealed the multi-grain morphology with induced porosity. The elemental composition of the prepared NBT ceramics was obtained by EDAX. The corresponding FTIR absorption peaks in NBT shifted due to Nd3+ ion doping. The diffuse reflectance spectroscopy (DRS) showed a decrease in the band gap due to the inhomogeneous spread out of the dopant in NBT. The photoluminescence spectroscopy reflected that the Commission International del’Eclairage (CIE) hue coordinates in neodymium-modified NBT appeared in the red region. The hysteresis loop at higher fields is symbolic of the ferromagnetic nature of the material. The ceramics that were examined exhibit low values of wear and friction coefficients.

chemistry, physical, inorganic & nuclear