Abstract:Because of its extreme hardness, wear resistance, good thermal conductivity and low thermal expansion coefficients, a diamond tool exhibits a range of properties which makes it a key and unique component in many fields of mechanical engineering. In comparison with the other types of diamond tools, the thin film diamond-coated cutting inserts have great potentialities in the commercial application because of its low costs for fabrication equipment and high performance. Thus, they are on the verge of becoming the next generation of tools used for high speed machining non-ferrous metals and alloys, metal-compound materials, and hard brittle non-metals. However, the poor adhesion of the diamond film on the substrate becomes the main technical barriers for the successful development and commercialization of diamond-coated tools. In this paper, diamond thin films were deposited on WC-Co cemented carbide substrates by the electron aided hot filament chemical vapor deposition (EACVD), using a mixture of hydrogen and acetone as source gases. A new multiple chemical pre-treatment including microwave oxidation, reaction in alkaline solution and cleaning by ultrasonic treatment in acid solution has been performed for free shape cemented WC-Co drills in order to increase the diamond nucleation and to enhance the coating adhesion. And also, another new pretreatment method using Ar-HZ gas etching decarburization by microwave plasma is performed for the WC-Co substrate surface. The influences of this pretreatment technique on the adhesion strength, diamond nucleation and surface morphology of the diamond thin film are investigated. Scanning electron microscope (SEM) was used to view the substrate morphology, and to examine the cobalt removal. After pre-treatment, the surface of the WC-Co substrate becomes slightly rough, but its composition and structure shows no changes identified by X-ray diffraction (XRD). Scanning electron microscope (SEM) indicates a distribution of uniform micro-roughness WC grains on substrate surface. And also the research results show that the pretreatment using Ar-H etching decarburization by microwave plasma is an effective method to enhance adhesive strength. The appropriate CVD processes were studied for the fabrication of tools with complex geometries. An adequate amount of additive can effectively prevent the overflow of Co from inner to surface of the substrate and avoid the catalytic effect of Co during CVD. The smooth diamond film with low surface roughness can be deposited by increasing the carbon source concentration and reducing the reactive pressure at the later stage of CVD process. The diamond morphology quality and homogeneity of coatings were characterized by SEM and Raman spectroscopy. The cutting performances of diamond-coated tools were studied by the cutting tests of difficult-to-machine materials. The research results show that the high quality diamond coating has been deposited on complex shape substrates for WC-Co cemented carbide twist drills. The cutting performances of diamond-coated drills are improved further by the new pretreatment and CVD process. It is of great significance for the fabrication and application of the diamond-coated tools with complex geometries.

Gas-jet MPCVD synthesis of diamond coatings on substrates of various materials

GAS-JET SYNTHESIS OF DIAMOND COATINGS ON SILICON SUBSTRATES FROM AN H2 + CH4 + Ar MIXTURE ACTIVATED IN A MICROWAVE DISCHARGE

Effect of methane flow rate on gas-jet MPCVD diamond synthesis

Effective cooling of substrates with low thermal conductivity under conditions of gas-jet MPCVD diamond synthesis

Microscopic properties of MPCVD diamond coatings studied by micro-Raman and micro-photoluminescence spectroscopy

Application of Raman Spectroscopy for Analyzing Diamond Coatings on a Hard Alloy

Using a Laser Plasmatron to Synthesize Diamond Coatings on a Carbide Cutting Tool

Very high growth rate chemical vapor deposition of single-crystal diamond.

Group growth of polycrystalline diamond coating by MPCVD technique on a hard alloy tool with a thin blade

Using active carbon pellet as substrate for deposition diamond by MPCVD

Uniform diamond coatings on WC-Co hard alloy cutting inserts deposited by a microwave plasma CVD

Morphologies and structures of chemical vapor deposited diamond films and film-substrate interfaces

Enhanced Nucleation and Growth of Diamond Film on Si by CVD Using a Chemical Precursor

Preparation of Ti-coated Diamond Particles by Microwave Heating

Synthesis and Mechanism Study of Carbon Nanowires, Carbon Nanotubes, and Carbon Pompons on Single-Crystal Diamonds

Growth of single-crystal diamond by microwave plasma CVD with high precursor utilization using cyclic gas injection and control of carbonaceous species content with optical emission spectroscopy

THE DEVELOPMENT OF MICROWAVE PLASMA CHEMICAL VOPOR DEPOSITION FACILITIES FOR DIAMOND FILMS

Mechanical properties of diamond like carbon coatings prepared by microwave electron cyclotron resonance plasma chemical vapour deposition process

Formation of Diamond-Like Carbon Coatings by Chemical Deposition in High Density Plasma

A New Multiple Chemical Pretreatment For Fabrication Of High Quality Cvd Diamond-Coated Drills

Investigation of diamond deposition on the diamond, silicon and quartz substrates by microwave plasma chemical vapor deposition and Monte Carlo simulations