Abstract:<p>The existing stereolithography-based ceramic 3D printing techniques are noncontinuous in a layer-by-layer method, which usually causes drawbacks of anisotropic mechanical properties, stair-casing effect, and the low fabrication rate. In this paper, a continuous DLP-based ceramic 3D printing is proposed to achieve the layerless ceramic manufacturing. In order to achieve this goal, a composite oxygen-rich film was designed with a microporous PET film and a PDMS coating to ensure a proper dead zone thickness according to the oxygen-controlled inhibition effect and low surface energy for releasing quickly from ceramic slurry. And a ceramic slurry with low viscosity was also prepared to match it. Then, the effects of influencing factors including the composite oxygen-rich film, ceramic slurry, and the print speed on the printing quality and geometrical overgrowth have been investigated. It shows that the geometrical overgrowth has a good linear relationship with this variable, the larger dead zone thickness, the higher solid content, and the low print speed, the larger the geometrical overgrowth. And the print speed does not worsen the surface quality. This proposed method can achieve the maximum speed of 143 mm/h and a surface roughness of 0.127 for a 40 vol% ceramic slurry. To demonstrate the utility of this system, parts of hollow structure, thin wall structure, and impeller structure have been successfully printed and sintered to ceramics with a condensed and porous structure. As a result, the proposed continuous DLP-based ceramic 3D printing technique provides a promising solution for ceramic 3D printing.</p>

Rapid and high-accuracy forming of ceramic parts by DLP technology based on optimization of shear stress

Manufacturing of a ceramic groove part based on additive and subtractive technologies

Mechanism of Ceramic Slurry Light Scattering Affecting Contour Accuracy and Method of Projection Plane Correction

Rapid Preparation and Performance of Degradable Ceramic Scaffolds Based on Stereolithography

Stereolithography-based additive manufacturing of lightweight and high-strength Cf/SiC ceramics

POLYMER-DERIVED SIC CERAMIC WITH TRIPLY PERIOD MINIMAL SURFACE STRUCTURE FABRICATION THROUGH DIGITAL LIGHT PROCESSING

Study on Forming Accuracy of ZrO2 Ceramic Materials Prepared by DLP Technology

Optimizing the properties of vat photopolymerization 3D-printed SiC ceramics by multi-infiltration

High-resolution multiceramic additive manufacturing based on digital light processing

Effect of Printing Strategies on Forming Accuracy and Mechanical Properties of ZrO2 Parts Fabricated by SLA Technology

Rapid Manufacturing Of Ceramic Parts

3D printing of dense structural ceramic microcomponents with low cost: Tailoring the sintering kinetics and the microstructure evolution

Formation mechanism and controlling strategy of lamellar structure in 3D printed alumina ceramics by digital light processing

Continuous DLP-based ceramic 3D printing using a composite oxygen-rich film

Hydrogel-based DLP 3D Printing of Dense Zirconia Ceramics

Design of a Shaping System for Stereolithography with High Solid Loading Ceramic Suspensions

Preparation of excellent performance ZTA ceramics and complex shaped components using digital light processing 3D printing technology

Supportability of a High-Yield-Stress Slurry in a New Stereolithography-Based Ceramic Fabrication Process

Direct fabrication process of ceramics based on stereolithography

Optimized Zirconia 3D Printing Using Digital Light Processing with Continuous Film Supply and Recyclable Slurry System