Abstract:Corrosion-fatigue is a significant design consideration in deepwater floating production systems. Mechanical loading is accentuated due to the compliant nature of these structures, and sour service conditions can also occur either due to the nature of the crude production or due to seawater flooding of the reservoir to enhance production yield. New high-strength riser steels have recently been developed to meet the demands of deepwater development. The objective of this study was to characterize the corrosion-fatigue resistance of these materials in terms of crack growth rates as a function of applied stress intensity factor range (ΔK), as well as cyclic loading frequency. Experiments were performed on five different steels with yield strengths ranging from 848 to 1080 MPa. Two environments were considered: seawater with cathodic protection to simulate the environment outside of the riser, and a sour brine environment with low oxygen (< 10 ppb) to simulate the environment inside the riser. Not all steels were tested in the sour brine environment since not all were designed to operate in sour service. For both environments, higher strength steels were found to exhibit higher growth rates and lower saturation frequencies. Fatigue crack growth rates as a function of ΔK were also measured, and exhibited two different frequency responses. At high ΔK, the classical frequency response occurred: decreased frequency gave increased crack growth rates. At low ΔK, an inverse frequency effect was observed: deceased frequency gave decreased crack growth rates, as well as increased corrosion-fatigue crack growth thresholds. These differences are believed to be caused by different underlying processes controlling crack growth — specifically, material-environment reaction kinetics at high ΔK, and crack closure due to corrosion-product wedging at low ΔK. The practical significance of these results is discussed, including selection of frequencies for corrosion-fatigue crack growth testing, and applicability of results to structural integrity assessments.

Effect of Frequency and Ratio of Wet/Dry Stages in Cyclic Corrosion Tests on Localized Corrosion of Complex-Phase High-Strength Steel

Effect Of Corroded Surface Morphology On Ultra-Low Cycle Fatigue Of Steel Bridge Piers

Ultra-low Cycle Fatigue Properties and Fracture Mechanism of Corroded Structural Steel

The Evolution of the Corrosion Mechanism of Structural Steel Exposed to the Urban Industrial Atmosphere for Seven Years

Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet-Dry Cycles in Chloride Environment.

Corrosion of Steel Embedded in Mortar and Concrete under Different Electrolytic Accelerated Corrosion Methods

Influence of Environment on the Development of Corrosion Product-Filled Paste and a Corrosion Layer at the Steel/concrete Interface

Study On Distribution Of Steel Corrosion Products In Concrete Structures

High-Temperature Mechanical Properties of Artificially Simulated Corroded Q500MC Structural Steel

Corrosion behavior of the low alloy weathering steels coupled with stainless steel in simulated open atmosphere

The Effect of Cyclic Loading Frequency on Corrosion-Fatigue Crack Growth in High-Strength Riser Materials

Correlativity on Indoor Accelerated Corrosion and Atmospheric Exposure of 430 Stainless Steel

Corrosion Micro- and Macro-Electrochemical Behavior of Rusted Carbon Steel and Weathering Steel

Enhancement in Corrosion Resistance of Low-Carbon Steel via Surface Modification

Fundamental understanding on the effect of Cr on corrosion resistance of weathering steel in simulated tropical marine atmosphere

Effect of Oxide Scale Microstructure on Atmospheric Corrosion Behavior of Hot Rolled Steel Strip

Mechanical and surface characterization of interstitial‐free steel corroded under wet‐dry salt spray and immersion conditions: A comparative study

Effect of Cu, Mn on the Corrosion Performance of Carbon Steels in Wet/Dry Environments

Mechanism in the Effect of External Stresses on the Oxidation and Scale Growth Kinetic of Steels under Cyclic Temperatures

Study on corrosion performance and corrosion product composition of weathering steel and high‐performance steel in simulated C3 environment

Effect of Organizational Evolution on the Stress Corrosion Cracking of the Cr-Co-Ni-Mo Series of Ultra-High Strength Stainless Steel