Abstract:Crevice corrosion in modular taper junctions of hip or knee replacements using cobalt-chrome-molybdenum (CoCrMo) alloys remains a clinical concern. Non-mechanically-driven corrosion has been less explored compared to mechanically assisted crevice corrosion. This study hypothesized that solution chemistry within crevices, inflammation, and cathodic electrode potential shifts during fretting result in low pH and generate reactive oxygen species (ROS), affecting oxide film behavior. This study investigated how resistance and capacitance of the CoCrMo oxide film (i.e., corrosion resistance) are modified in simulated in vivo crevice environments of modular taper junctions. Six solutions were evaluated (two pH levels: 1 and 7.4 and four hydrogen peroxide (H2O2) concentrations: 0, 0.001, 0.01 and 0.1 M). Rp versus voltage and Mott-Schottky plots were created from symmetry-based electrochemical impedance spectroscopy (sbEIS). At pH 1, the semiconductor transition to p-type occurs at more anodic potentials and higher flat band potentials were found. H2O2 decreased the flat band potential and slope in the Mott-Schottky plot. Higher H2O2 in pH 7.4 solution significantly modified the oxide film, leading to increased donor density (p = 0.0004) and a 150-fold reduction in Rp in the cathodic potential range at -1 V (p = 0.0005). The most unfavorable condition (0.1 M H2O2 pH 1) resulted in a 250-fold lower resistance compared to phosphate buffered saline (PBS) pH 7.4 at -1 V (p = 0.0013). This study highlights the corrosion susceptibility of CoCrMo under adverse chemical and potential conditions, identifying increased defects in the oxide film due to ROS, hydrogen ions and electrode potential. STATEMENT OF SIGNIFICANCE: : Corrosion of cobalt chrome molybdenum alloy caused by direct chemical attack in the crevice region of hip replacements, such as modular taper junctions, remains a clinical concern. The junction environment contains adverse chemical compositions, including high acidity and reactive oxygen species (ROS) due to inflammatory responses against the corrosion products. We simulate inflammatory environments with different pH levels and hydrogen peroxide, representative of ROS. We employ electrochemical impedance spectroscopy and apply stepwise voltage over the range induced by tribocorrosion processes. We relate the effect of adverse chemical components on corrosion and semiconducting behavior of the oxide film using Mott-Schottky analysis. This study shows how pH and ROS concentration compromises the oxide film potentially leading to non-mechanically induced corrosion.

Corrosion Behavior of Electrolytic CoRe Alloys Under Exposure to an Alkaline Medium

Microstructure and Corrosion Resistance of Medical Cobalt-Based Alloys

Influence of the Contents of Refractory Components on the Corrosion Resistance of Ternary Alloys Based on Iron and Cobalt

The Influence of the Composition of Amorphous Alloys on Their Corrosion Resistance in Aggressive Environments of Different Nature

Reactive Oxygen Species, Electrode Potential and pH Affect CoCrMo Alloy Corrosion and Semiconducting Behavior in Simulated Inflammatory Environments

Anodic Behavior of AK7 Aluminum Alloy and Composite Material of the Al–Al2O3 System within an NaCl Electrolyte Solution Medium

Corrosion Behavior of Aluminum Alloys in Different Alkaline Environments: Effect of Alloying Elements and Anodization Treatments

Corrosion behavior and electrochemical properties of carbon steel, commercial pure titanium, copper and copper–aluminum–nickel alloy in 3.5% sodium chloride containing sulfide ions

PECULIARITIES OF ELECTRODEPOSITION OF COBALT—WOLFRAM—RENIUM ALLOY

Study of Corrosion-Electrochemical Behavior of Aluminum-Beryllium Alloys Alloyed with Yttrium, Lanthanum and Cerium

Relationship of Corrosion Behavior Between Single-Phase Equiatomic CoCrNi, CoCrNiFe, CoCrNiFeMn Alloys and Their Constituents in NaCl Solution

The Influence of Co Content and Sintering Time in Al–Al9Co2–Al13Co4 Composites on Microstructure and Corrosion Performance in NaOH Environment

Corrosion Behavior of Pure Zinc and Its Alloy under Thin Electrolyte Layer

Kinetics and mechanism of corrosion of oxide coating fabricated on aluminum alloy by the plasma electrolytic oxidation in molten salt

The corrosion behavior of electroless Ni–P coatings in concentrated KOH electrolyte

Corrosion Mechanism and Electrochemical Reactions on Alloy 690 in Simulated Primary Coolant of Water–Water Energy Reactors

Corrosion behavior of AlNiCoCuZr high-entropy equiatomic alloy in NaCl solution

Corrosion Behavior of Titanium Alloys (Ti CP2, Ti-6Al-2Sn-4Zr-2Mo, Ti-6Al-4V y Ti Beta-C) with Anodized and Exposed in NaCl and H2SO4 Solutions

Corrosion and electrochemical behavior of CoСrFeNiMo high-entropy alloy in acidic oxidizing and neutral chloride solutions

Corrosion Resistance, Composition, and Stratification of Passive Films: Ni-22Cr and Ni-22Cr-6Mo Alloys Passivated and Exposure Aged in Acidic Chloride Solutions

Electrochemical Corrosion Behavior of Biomedical Ti–22Nb and Ti–22Nb–6Zr Alloys in Saline Medium