Abstract:Material extrusion (MEX) of high-filled polymers with metal or ceramic powders has showed great potential in fabricating 3D structure combined via the powder metallurgy route. However, defects between deposited layers adversely affect the final performance of 3D components. Here, we introduced a high-flow filling approach based on effective viscosity control and optimized printing strategies for preparing high-density NiFe2O4-based cermet. We investigated the influence of powder loading and filling paths on both green and sintered samples regarding density, microstructure and mechanical properties. Polyformaldehyde (POM)-based feedstocks were developed with powder loading of 62 vol% and 56 vol%. 3D cermet with high powder loading demonstrated good shape retention but contained periodic pores due to low-flow filling between adjacent filament. Cermets with high relative density were achieved using 56 vol% POM-based feedstock because of satisfactory fluidity and high-filling effect during deposition. Filling paths determined the distribution and size of the pores, with cermet based on the (45°, 135°) trace exhibiting the most uniform and dense structure. Cermets using 62 vol% feedstock showed significant differences in flexural strength depending on the filling path, much lower than those achieved with the high-flow filling approach. Finally, 3D NiFe2O4-based cermets utilizing 56 vol% feedstock demonstrated an optimal average flexural strength of 173.5 MPa, close to 178.4 MPa of conventional injection molded samples. Hence, high-qualified metal-ceramic composites can be fabricated using MEX via the high-flow filling approach, with potential applications in complex-shaped anode, cutting tools and wear-resistant parts.

Complex-shaped TiC/Ti(C,N)-based cermet prepared via rheological press molding using highly-filled granular feedstock

Plastic shaping of NiFe2O4‐based cermets using granular feedstock: microstructure and mechanical properties

Enhanced Densification of Ultrafine Ti(C, N)-based Cermets Based on Grain-Growth Induced Liquid-Phase Pore Filling Mechanism

Submicron Ti(C,N)-based cermets with improved microstructure using high-energy milled and subsequent heat-treated ultrafine Ti(C,N) powders

Strong and densified 3D metal-ceramic composite with strengthened layer structure by material extrusion additive manufacturing

The production of in situ (Mo,Ti)(C,N)-based cermets without a core/rim structure by reaction hot pressing: Formation mechanism and mechanical properties

Microstructure and properties of Ti(C, N)-based cermet with multi-core-rim microstructure: effect of (Ti, W, Ta) (C, N) pre-solid solution composition

Evolution of microstructure and interfacial characteristics of complete solid-solution Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Fabrication, microstructure evolution, and mechanical properties of Ti(C,N)-HfN-WC-Ni-Mo cermets

Fabrication and properties of TiC-high manganese steel cermet processed by 3D gel printing

Microstructure and Properties of Gradient Ti(C,N)-Based Cermets by Powder Extrusion Additive Manufacturing

Fast Preparation of ZTA-TiC-FeCrNi Cermets by High-Gravity Combustion Synthesis

Tuning microstructure for superb mechanical properties in a Ti(C,N)-(WMoTaNbTi)C-Ni/Co cermets via change sintering temperature

DENSE TiC-Al2O3-Fe CERMET FABRICATED BY SHS

Effect of ZrO2 Whiskers on the Microstructure and Mechanical Properties of a Ti(C,N)‐based Cermet Cutting Tool Material

Preparation, mechanical properties and enhanced wear resistance of TiC-Fe composite cermet coating

Fabrication of large cross-section Ti–6Al–4V alloy using EBS-modified POM-based feedstock

Preparation and properties of Ti(C,N)-based cermets with graphene nanosheet addition by spark plasma sintering

Achieving hardness‐strength‐toughness synergy in (Ti, W, Mo, Cr)(C, N)‐based cermets

Dual-grained Mo2FeB2-based cermets containing WC fabricated via multi-step sintering approach: Microstructure, mechanical properties and interface characteristics

Effects of CrMnFeCoNi additions on microstructure, mechanical properties and wear resistance of Ti(C,N)-based cermets