Unraveling the Origin of Donor‐Like Effect in Bismuth–Telluride‐Based Thermoelectric Materials

Feng Liu,Min Zhang,Pengfei Nan,Xin Zheng,Yuzheng Li,Kang Wu,Zhongkang Han,Binghui Ge,Xinbing Zhao,Chenguang Fu,Tiejun Zhu

DOI: https://doi.org/10.1002/smsc.202300082

2023-08-10

Small Science

Abstract:The donor‐like effect, depicting the uncontrollable increase of electron density that can significantly alter the thermoelectric performance of both p‐type and n‐type polycrystalline Bi 2 Te 3 ‐based materials, has long been an intriguing phenomenon, while its origin is still elusive. Herein, it is found that different from the common argument, the donor‐like effect in Bi 2 Te 3 ‐based polycrystals is a result of the oxygen‐adsorption‐induced evolution of the point defects. The dominant point defect in stoichiometric zone‐melted Bi 2 Te 3 ingot is the acceptor‐like . During the fabrication of high‐strength polycrystals, the exposure of the powders to the air leads to their absorption of oxygen and the formation of secondary phase Bi 2 TeO 5 in the following sintering process. This brings about a change of local chemical equilibrium and promotes the evolution of the intrinsic point defect from acceptor‐like to donor‐like . Notably, if the fabrication process is strictly controlled to minimize oxygen adsorption, the evolution of the point defects will be avoided, whereby the donor‐like effect disappears. Consequently, a reproducible high zT value of 1.0 at 325 K can be achieved in Bi 2 Te 2.7 Se 0.3 ‐based polycrystals. These results highlight the importance of understanding the evolution of point defects, which is crucial for developing high‐performance Bi 2 Te 3 ‐based polycrystals and corresponding fabrication processes.