Synergistic effects of B-In codoping in zone-melted Bi0.48Sb1.52Te3-based thermoelectric

Hongxiang Wang,Gang Wu,Zipeng Yan,Xiaojian Tan,Jianfeng Cai,Haoyang Hu,Peng Sun,Guoqiang Liu,Jun Jiang

DOI: https://doi.org/10.1016/j.cej.2021.130381

IF: 15.1

2021-09-01

Chemical Engineering Journal

Abstract:Bismuth-telluride-based alloys are the unique commercial thermoelectric materials near room temperature, and the commonly used zone-melting method is efficient for the mass production. Since the ZTs of zone-melted samples has stagnated around 1.2 for decades, it is urgent for the scientific and industrial societies to break through this bottleneck. Herein, we report simultaneously improved power factor and ZT values in p-type Bi0.48Sb1.52Te3 materials by the addition of amorphous boron and metal indium. B and In dopants not only effectively increase the hole concentration and the density of state effective mass, leading to a high power factor of 55 μW cm−1 K−2, but also introduce various phonon scattering centers to obviously suppress the lattice thermal conductivity. The synergistic effects yield a ZT max of 1.45 at 350 K, as well as a ZT ave of 1.20 and σS 2 ave of 41 μW cm−1 K−2 (300 ~ 500 K) in the Bi0.48Sb1.515In0.005Te3 + 0.6 wt% B sample, suggesting tiny B-In codoping is a promising strategy for the further development of bismuth telluride thermoelectrics.

engineering, chemical, environmental

What problem does this paper attempt to address?

The paper is primarily dedicated to addressing the issue of enhancing the thermoelectric performance of bismuth antimony telluride-based thermoelectric materials (Bi0.48Sb1.52Te3) near room temperature. Specifically, the paper introduces amorphous boron (B) and indium (In) as co-dopants in the zone-melted Bi0.48Sb1.52Te3 material, aiming to simultaneously improve the power factor (σS^2) and the thermoelectric figure of merit (ZT).

The paper points out that although the zone-melted Bi0.48Sb1.52Te3 material has been widely used in commercial thermoelectric applications, its ZT value has stagnated around 1.2 for many years. Therefore, the focus of the research is on using co-doping methods to not only increase the ZT value but also enhance the power factor, thereby achieving better thermoelectric conversion efficiency and output power. Through this method, the researchers successfully increased the maximum ZT value to 1.45, and the average ZT value in the range of 300 to 500 K reached 1.20, significantly better than the undoped samples. Additionally, co-doping also improved the mechanical properties of the material, such as Vickers hardness.