High‐Performance Industrial‐Grade p‐Type (Bi,Sb)2Te3 Thermoelectric Enabled by a Stepwise Optimization Strategy
Qiang Zhang,Minhui Yuan,Kaikai Pang,Yuyou Zhang,Ruoyu Wang,Xiaojian Tan,Gang Wu,Haoyang Hu,Jiehua Wu,Peng Sun,Guo‐Qiang Liu,Jun Jiang
DOI: https://doi.org/10.1002/adma.202300338
IF: 29.4
2023-03-04
Advanced Materials
Abstract:As the sole dominator of the commercial thermoelectric (TE) market, Bi2Te3‐based alloys play an irreplaceable role in Peltier cooling and low‐grade waste heat recovery. At present, the main barrier to a wider application is the relatively low efficiency determined by the low‐rise TE figure of merit ZT. Herein, an effective approach is reported for improving the TE performance of p‐type (Bi,Sb)2Te3 by incorporating Ag8GeTe6 and Se. Specifically, the diffused Ag and Ge atoms into the matrix conduce to optimized carrier concentration and enlarged the density of states effective mass while the Sb‐rich nanoprecipitates generate coherent interfaces with little loss of carrier mobility. The subsequent Se dopants introduce multiple phonon scattering sources and significantly suppress the lattice thermal conductivity while maintaining a decent power factor. Consequently, a high peak ZT of 1.53 at 350 K and a remarkable average ZT of 1.31 (300−500 K) are attained in the Bi0.4Sb1.6Te0.95Se0.05 + 0.10 wt% Ag8GeTe6 sample. Most noteworthily, the size and mass of the optimal sample have been enlarged to Ø40 mm‐200 g and the constructed 17‐couple TE module exhibits an extraordinary conversion efficiency η of 6.3% at ΔT = 245 K. This work demonstrates a facile method to develop high‐performance and industrial‐grade (Bi,Sb)2Te3‐based alloys, which paves a strong way for the further practical applications. This article is protected by copyright. All rights reserved
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology