Coral-like Li 7 La 3 Zr 2 O 12 -Filled PVDF-HFP/LiODFB Composite Electrolytes for Solid-State Batteries with Excellent Cycle Performance
Shengdong Tao,Jian Li,Lihua Wang,Weiguo Huang,Minchao Zhang,Zhexi Chi,Shuohan Wang,Yongzhi Chen,Lei Shang
DOI: https://doi.org/10.1021/acsaem.1c02217
IF: 6.4
2021-10-04
ACS Applied Energy Materials
Abstract:Development of an active filler with a large specific surface area, fast ion conductivity phase, special shape, and high electrochemical stability is a critical issue for prominent performance composite solid-state electrolytes (CSEs) in solid-state lithium-ion batteries. Here, we report large specific surface area and coral-like cubic Li7La3Zr2O12 (LLZO) that was synthesized via a metal–organic framework (MOF) at a low calcination temperature (1000 °C). As active fillers, the coral-like cubic LLZO and lithium oxalyldifluroborate (LiODFB) uniformly distributed in a poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) matrix provide an interconnected Li-ion transport channel in CSE, which manifests outstanding properties such as a favorable electrochemical stability window (of 4.85 V vs Li/Li+), high ionic conductivity (1.65 × 10–4 S cm–1, 20 °C), and superior interface compatibility with lithium metal. The assembled LiFePO4/CSE/Li and LiCoO2/CSE/Li cells convey predominate performance and initial specific capacities of 135.0 and 135.9 mA h g–1 at 0.5 C, with capacity retention values of 83.51% after 500 cycles and 93.90% after 200 cycles. The coral-like LLZO with a large specific area reduces polymer crystallinity and provides a large phase interface in CSE through interaction of LLZO with LiODFB and PVDF-HFP. The results suggest that coral-like LLZO prepared by MOFs is a promising filler in CSEs for solid-state lithium-ion batteries.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.1c02217.S1 and S2, detailed preparation process of LLZO-B and LLZO-P; Figure S1, SEM images of LLZO-P, LLZO-S, and LLZO-B; Figure S2, SEM images of the cross section of CSEs and elemental mapping images of PLLP; Figure S3, HR-TEM images of LLZO samples; Figure S4, FT-IR spectra of PVDF-HFP, PL, and CSEs; Figure S5, Nyquist plots and ionic conductivity of PPLP, PPLS, and PPLB; Figure S6, enlarged view of voltage–time curves in Li//Li cells; Figure S7, charge and discharge curves of cells at different cycles; Figure S8, cycle performances and curves of NCM811//Li cells; Figure S10, SEM image of the Li film in cycled cells; Figure S11, ionic conductivity and Nyquist curves of PLLP with different contents of LLZO-P; Figure S12, lithium-ion migration number of CSEs; and Figures S13 and S14, C-rate and cycle performance of LiFePO4 battery with PLLB and PLLS (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels