A promising composite solid electrolyte incorporating LLZO into PEO/PVDF matrix for all-solid-state lithium-ion batteries

Jun Li,Kongjun Zhu,Zhongran Yao,Guoming Qian,Jie Zhang,Kang Yan,Jing Wang

DOI: https://doi.org/10.1007/s11581-019-03320-x

IF: 2.961

2019-11-10

Ionics

Abstract:<p class="a-plus-plus">Solid electrolytes should be sought to exhibit high conductivity, good thermostability, and excellent mechanical properties for realizing excellent performance of lithium-ion batteries. In this study, we optimize the composition of poly(ethylene oxide)/poly(vinylidene fluoride) (PEO/PVDF) matrix and introduce Li<sub class="a-plus-plus">6.2</sub>Ga<sub class="a-plus-plus">0.1</sub>La<sub class="a-plus-plus">3</sub>Zr<sub class="a-plus-plus">1.5</sub>Bi<sub class="a-plus-plus">0.5</sub>O<sub class="a-plus-plus">12</sub> (LLZO) ceramic powders into the matrix to form novel composite solid electrolytes. The PEO/PVDF blend matrix shows a low melting point and crystallinity and a high thermostability when the weight ratio of PEO and PVDF is 7:3. The electrolyte consisting of this PEO/PVDF blend matrix and 10 wt% LLZO shows the maximum conductivity (4.2 × 10<sup class="a-plus-plus">−5</sup> S cm<sup class="a-plus-plus">−1</sup> at 30 °C). In addition, all-solid-state LiFePO<sub class="a-plus-plus">4</sub>||Li battery assembled with this solid electrolyte shows good cycling stability, which retained 96.5% of the maximum capacity after 100 cycles, and columbic efficiency (close to 100%) at 60 °C. The Li||Li symmetric battery assembled with the solid electrolyte can be steadily cycled for more than 300 h at a current density of 0.2 mA cm<sup class="a-plus-plus">−2</sup> at 60 °C. Hence, the new as-synthesized solid electrolyte should be a promising electrolyte for high performance of all-solid-state batteries.</p>

chemistry, physical,physics, condensed matter,electrochemistry

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to realize a solid electrolyte with high conductivity, good thermal stability and excellent mechanical properties in all - solid - state lithium - ion batteries. Specifically, the author overcomes the deficiencies of traditional polymer electrolytes in conductivity, mechanical strength and thermal stability by optimizing the composition of the polyethylene oxide/polyvinylidene fluoride (PEO/PVDF) matrix and introducing lithium lanthanum zirconium oxide (LLZO) ceramic powder to form a new type of composite solid electrolyte. These improvements aim to enhance the overall performance of all - solid - state lithium - ion batteries, including cycle stability and coulombic efficiency. The paper verifies the effectiveness and potential of this new type of composite solid electrolyte in practical applications through experiments.