Abstract:An initially single phase high entropy alloy (HEA) Al0.3CoCrFeNi was irradiated by 3 MeV Au ions to a fluence of 6 x 10(15) cm(2) (similar to 31 dpa at damage peak) at four different temperatures ranging from 250 degrees C to 650 degrees C. Transmission electron microscopy (TEM) and Atom probe tomography (APT) were employed to study the evolution of structural damage and phase stability with irradiation temperature. Al0.3CoCrFeNi exhibited a similar evolution of irradiation-induced defects with temperature as compared with conventional FCC alloys. At 250 degrees C and 350 degrees C, most of the visible irradiation-induced defects were faulted 1/3(111) dislocation loops. As the irradiation temperature increased to 500 degrees C, perfect 1/2(110) dislocation loops were observed along with the faulted loops. At the highest irradiation temperature 650 degrees C, only dislocation lines and networks could be observed. Regarding phase stability, the 3 MeV Au irradiation was observed to suppress the precipitation of (Ni, Al)-enriched nano clusters and the L12 ordered structure at irradiation temperatures 250 degrees C to 500 degrees C whereas precipitation of the B2 ordered structure was accelerated at 650 degrees C. This resulted in qualitatively opposite precipitation behavior between the ion irradiated damage region and unirradiated region at 500 degrees C and 650 degrees C. The opposite phase stability of the ion-irradiated damage region and unirradiated region at different temperatures is attributed to the competing effects of ballistic dissolution vs irradiation enhanced diffusion on precipitation. (C) 2020 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Effect of Au-ions irradiation on microstructure and mechanical properties of FeCrAl coating

Effect of Au-ions irradiation on mechanical and LBE corrosion properties of amorphous AlCrFeMoTi HEA coating: Enhanced or deteriorated?

Effect of Au-ion irradiation on the surface morphology, microstructure and mechanical properties of amorphous AlCrFeMoTi HEA coating

Au ion irradiation effects on microstructure and deuterium permeation resistance of Al/Al 2 O 3 coating

Microstructure response and LBE corrosion behavior of the FeCrAlY coating after Au-ions irradiation

Corrosion behavior of the FeCrAl coating with different Cr and Al contents before and after Au-ions irradiation in stagnant LBE

Effect of Au ion irradiation on the surface morphology, microstructure and mechanical properties of AlNbTiZr medium-entropy alloy coatings with various Al content for ATF

Irradiation effects on microstructure, mechanical properties, and lead-bismuth eutectic corrosion resistance of alumina coating

Dislocation loops and hardening induced by Au ion irradiation in FeCrAl alloys with three solute concentrations

Effect of Au-ion irradiation on the microstructure and deuterium permeation resistance of the Al2O3 prepared by the MOD method

Effects of Fe-Ions Irradiation on the Microstructure and Mechanical Properties of FeCrAl-1.5wt.% ZrC Alloys

Evolution of microstructure and mechanical properties of ZrC reinforced FeCrAl alloy after Fe-ions irradiation

Effect of Au-ion irradiation on the morphology, microstructure and lead-bismuth eutectic corrosion behavior of refractory TiNbZrMoV high-entropy alloy coating

Structural Damage and Phase Stability of Al0.3CoCrFeNi High Entropy Alloy under High Temperature Ion Irradiation

Microstructure response and lead-bismuth eutectic corrosion behavior of 11Cr1Si ferritic/martensitic steel after Au-ion irradiation

Effect of ultrasonic field on the friction and oxidation characteristics of FeCrAl Coatings

Effect of Cr on solidification structure and microhardness of Al-Ni alloy

Effects of Irradiation Temperature and Dose Rate on the Mechanical Properties of Self-Ion Implanted Fe and Fe-Cr Alloys

Effect of low-dose Xe20+ ion irradiation on the deformation behavior of the magnetron sputtered Cr coatings under nanoindentation

Irradiation Effects in Ni–17Mo–7Cr Alloy Bombarded with MeV Au Ions

Microstructure and radiation stability of nano-dispersoids in particle-reinforced FeCrAl alloys with different Zr concentrations