Abstract:A new three-step method for preparing aluminum rich coating on HR-2 stainless steel was proposed, i.e. ambient temperature chloroaluminate melts electroplating followed by heat treating and artificial oxidation. In the electroplating process, aluminum deposition from AlCl3/MEIC to the surface of HR-2 steel was performed with a deposition rate of 15 mu m/h. Within the aluminizing temperature range from 650 to 750 degrees C, aluminizing time from 1 to 30 h, the aluminized coating with thickness of 3-27 mu m can be prepared, which is homogeneous and free of porosity or crack, and have good metallographic adherence to the substrate; the coating cross section exhibits a three-layer or two-layer structure. A simple Arrhenius relationship can be used to describe the effect of temperature on the coating growth rate, which gives activation energy of 116.9 kJ/mol. The relationship between the coating thickness against time(1/2) is approximately linear, which is a typical feature of the diffusion controlled coating growth mechanism. To form Al2O3 film on surface, the aluminized coating treated for 4 h was oxidized in 10(-2) Pa O-2 for 80 h and observed by X-ray photoelectron spectroscopy (XPS) and Reflection spectrum. The finally fabricated coating shows a double-layer structure consisting of an outer gamma-Al2O3 layer with thickness of 110 nm and inner (Fe,Cr,Mn and Ni)Al/(Fe,Cr,Mn and Ni)(3)Al layer of 30 mu m thickness, and is homogeneous without any defects. The deuterium permeation rate through the coated HR-2 steel is reduced by 3 orders of magnitude at 600 degrees C. The coating remains a perfect surface for 20 thermal cycles between 750 degrees C and room temperature. The method is a potential candidate for preparation of TPB on the tritium container surface in ITER.

Effect of Au-ion irradiation on the microstructure and deuterium permeation resistance of the Al2O3 prepared by the MOD method

Au ion irradiation effects on microstructure and deuterium permeation resistance of Al/Al 2 O 3 coating

Effect of Au-ions irradiation on mechanical and LBE corrosion properties of amorphous AlCrFeMoTi HEA coating: Enhanced or deteriorated?

Irradiation effects on microstructure, mechanical properties, and lead-bismuth eutectic corrosion resistance of alumina coating

Effect of Au-ions irradiation on microstructure and mechanical properties of FeCrAl coating

Effect of Au ion irradiation on the surface morphology, microstructure and mechanical properties of AlNbTiZr medium-entropy alloy coatings with various Al content for ATF

Corrosion behavior and failure mechanism of amorphous Al2O3 coating at high-temperature LBE

Irradiation Effects on the Retention of Hydrogen in Al2o3

Effect of Au-ion irradiation on the surface morphology, microstructure and mechanical properties of amorphous AlCrFeMoTi HEA coating

Effect of 5 MeV Au3+ ions irradiation damage on surface blistering and deuterium retention behaviors in W and W-ZrC alloy

Microstructure response and LBE corrosion behavior of the FeCrAlY coating after Au-ions irradiation

Effect of Au-ion irradiation on the morphology, microstructure and lead-bismuth eutectic corrosion behavior of refractory TiNbZrMoV high-entropy alloy coating

A new preparing method and performances of FeAl/Al2O3 tritium permeation barrier

Effects of ion irradiation on chromium coatings of various thicknesses on a zirconium alloy

Microstructure Evolution and Effect on Deuterium Retention in Oxide Dispersion Strengthened Tungsten During He+ Irradiation

Surface Modification and Deuterium Retention of High Energy Rate Forging W-Y2O3exposed to Deuterium Plasma

Absolute radiation tolerance of amorphous alumina coatings at room temperature

Dislocation loops and hardening induced by Au ion irradiation in FeCrAl alloys with three solute concentrations

Improving hydrogen isotope permeation resistance of (TiVAlCrZr)O multi-component metal oxide coating by O + Ion implantation

Aluminum phosphate sealing to improve deuterium permeation resistance of α-Al2O3 coating prepared by MOD method

Microstructure and deuterium retention after ion irradiation of W–Lu2O3 composites