Abstract:An initially single phase high entropy alloy (HEA) Al0.3CoCrFeNi was irradiated by 3 MeV Au ions to a fluence of 6 x 10(15) cm(2) (similar to 31 dpa at damage peak) at four different temperatures ranging from 250 degrees C to 650 degrees C. Transmission electron microscopy (TEM) and Atom probe tomography (APT) were employed to study the evolution of structural damage and phase stability with irradiation temperature. Al0.3CoCrFeNi exhibited a similar evolution of irradiation-induced defects with temperature as compared with conventional FCC alloys. At 250 degrees C and 350 degrees C, most of the visible irradiation-induced defects were faulted 1/3(111) dislocation loops. As the irradiation temperature increased to 500 degrees C, perfect 1/2(110) dislocation loops were observed along with the faulted loops. At the highest irradiation temperature 650 degrees C, only dislocation lines and networks could be observed. Regarding phase stability, the 3 MeV Au irradiation was observed to suppress the precipitation of (Ni, Al)-enriched nano clusters and the L12 ordered structure at irradiation temperatures 250 degrees C to 500 degrees C whereas precipitation of the B2 ordered structure was accelerated at 650 degrees C. This resulted in qualitatively opposite precipitation behavior between the ion irradiated damage region and unirradiated region at 500 degrees C and 650 degrees C. The opposite phase stability of the ion-irradiated damage region and unirradiated region at different temperatures is attributed to the competing effects of ballistic dissolution vs irradiation enhanced diffusion on precipitation. (C) 2020 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Effect of Au-ions irradiation on mechanical and LBE corrosion properties of amorphous AlCrFeMoTi HEA coating: Enhanced or deteriorated?

Effect of Au-ions irradiation on microstructure and mechanical properties of FeCrAl coating

Effect of Au-ion irradiation on the surface morphology, microstructure and mechanical properties of amorphous AlCrFeMoTi HEA coating

Corrosion behavior of the FeCrAl coating with different Cr and Al contents before and after Au-ions irradiation in stagnant LBE

Au ion irradiation effects on microstructure and deuterium permeation resistance of Al/Al 2 O 3 coating

Corrosion behavior and failure mechanism of amorphous Al2O3 coating at high-temperature LBE

Microstructure response and LBE corrosion behavior of the FeCrAlY coating after Au-ions irradiation

Effect of Au-ion irradiation on the morphology, microstructure and lead-bismuth eutectic corrosion behavior of refractory TiNbZrMoV high-entropy alloy coating

Effect of Au-ion irradiation on the microstructure and deuterium permeation resistance of the Al2O3 prepared by the MOD method

Irradiation effects on microstructure, mechanical properties, and lead-bismuth eutectic corrosion resistance of alumina coating

Effect of Au ion irradiation on the surface morphology, microstructure and mechanical properties of AlNbTiZr medium-entropy alloy coatings with various Al content for ATF

Microstructure response and lead-bismuth eutectic corrosion behavior of 11Cr1Si ferritic/martensitic steel after Au-ion irradiation

Influence of coating thickness on microstructure, mechanical and LBE corrosion performance of amorphous AlCrFeTiNb high-entropy alloy coatings

Dislocation loops and hardening induced by Au ion irradiation in FeCrAl alloys with three solute concentrations

Structural Damage and Phase Stability of Al0.3CoCrFeNi High Entropy Alloy under High Temperature Ion Irradiation

Effects of ion irradiation on chromium coatings of various thicknesses on a zirconium alloy

Influence of Si addition on the microstructure, mechanical and lead-bismuth eutectic corrosion properties of an amorphous AlCrFeMoTiSix high-entropy alloy coating

Effect of annealing on corrosion resistance and mechanical properties of Cr–Fe–Ni–Co–Mo–Si–B amorphous coating

Microstructure, mechanical properties and lead-bismuth eutectic corrosion behavior of FeCrAlTiNb high-entropy alloy coatings

The effect of amorphous coating on high temperature oxidation resistance of Ni-based single crystal superalloy

Effect of LBE corrosion on microstructure of amorphous Al2O3 coating by magnetron sputtering