Abstract:In this study structural and mechanical properties of a 1 um thick Al2O3 coating, deposited on 316L stainless steel by Pulsed Laser Deposition (PLD), subjected to high energy ion irradiation were assessed. Mechanical properties of pristine and ion-modified specimens were investigated using the nanoindentation technique. A comprehensive characterization combining Transmission Electron Microscopy and Grazing-Incidence X-ray Diffraction provided deep insight into the structure of the tested material at the nano- and micro- scale. Variation in the local atomic ordering of the irradiated zone at different doses was investigated using a reduced distribution function analysis obtained from electron diffraction data. Findings from nanoindentation measurements revealed a slight reduction in hardness of all irradiated layers. At the same time TEM examination indicated that the irradiated layer remained amorphous over the whole dpa range. No evidence of crystallization, void formation or element segregation was observed up to the highest implanted dose. Reported mechanical and structural findings were critically compared with each other pointing to the conclusion that under given irradiation conditions, over the whole range of doses used, alumina coatings exhibit excellent radiation resistance. Obtained data strongly suggest that investigated material may be considered as a promising candidate for next-generation nuclear reactors, especially LFR-type, where high corrosion protection is one of the highest prerogatives to be met.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to evaluate the radiation tolerance of amorphous alumina coatings at room temperature, especially the changes in structural and mechanical properties under high - energy ion irradiation conditions. Specifically, the research aims to: 1. **Evaluate the changes in mechanical properties**: Measure the hardness of unirradiated and ion - irradiated samples by nanoindentation technology to understand the influence of irradiation on the hardness of the material. 2. **Analyze the structural changes**: Combine Transmission Electron Microscopy (TEM) and Grazing - Incidence X - ray Diffraction (GIXRD) to deeply study the microstructural changes of the irradiated material. 3. **Explore the changes in local atomic ordering**: Use the reduced distribution function analysis obtained from electron diffraction data to study the changes in local atomic ordering under different irradiation doses. The main purpose of the research is to verify the excellent radiation tolerance of alumina coatings under high - energy ion irradiation conditions and provide theoretical basis and technical support for the application in the next - generation nuclear reactors (especially the Lead - cooled Fast Reactor, LFR). These reactors require materials to have extremely high corrosion resistance and structural stability, especially under high - temperature and high - irradiation conditions. In summary, the key problems that this research attempts to solve are: - Will the structural and mechanical properties of alumina coatings change significantly under high - energy ion irradiation? - Will these changes affect their applicability as protective coatings for the new - generation nuclear reactors? Through these studies, the author hopes to provide an important reference for the selection of future nuclear reactor materials and promote the development of related technologies.

Absolute radiation tolerance of amorphous alumina coatings at room temperature

Study of amorphous alumina coatings for next-generation nuclear reactors: High-temperature in-situ and post-mortem Raman spectroscopy and X-ray diffraction

Corrosion behavior and failure mechanism of amorphous Al2O3 coating at high-temperature LBE

High versus low energy ion irradiation impact on functional properties of PLD-grown alumina coatin

Mechanical behavior of ion-irradiated ODS RAF steels strengthened with different types of refractory oxides

Irradiation effects on microstructure, mechanical properties, and lead-bismuth eutectic corrosion resistance of alumina coating

Irradiation resistance of vacuum arc chromium coatings for zirconium alloy fuel claddings

Effect of Au-ion irradiation on the microstructure and deuterium permeation resistance of the Al2O3 prepared by the MOD method

Au ion irradiation effects on microstructure and deuterium permeation resistance of Al/Al 2 O 3 coating

Comparative study on the effects of α/γ phase ratio on the micro-structures and properties in Al2O3 coatings under silicon ion irradiation

A novel plasma-sprayed Cr/FeCrAl dual-layer coating on Zr alloy for potential high‐temperature applications

Evaluation of Fracture Toughness of Plasma Electrolytic Oxidized Al2O3-ZrO2 Coatings Utilizing Nano-Scratch Technique

Microstructure response and LBE corrosion behavior of the FeCrAlY coating after Au-ions irradiation

Experimental evaluation of cold spray FeCrAl alloys coated zirconium-alloy for potential accident tolerant fuel cladding

Study of the Relationship between Changes in the Structural, Optical, and Strength Properties of AlN Ceramics Subjected to Irradiation with Heavy Xe23+ Ions

Radiation-Induced Sharpening in Cr-Coated Zirconium Alloy

Predicting the Residual Stress of Amorphous Al2O3-Y2O3 Nano-Laminated Deuterium Permeation Barrier under Thermal Cycles

Effect of Surface Modification on Erosion Behavior of Alumina-Samarium Strontium Aluminate Composite Thermal Barrier Coatings

Atom probe tomography characterization of high-dose ion irradiated MA957

Effect of residual impurities on the behavior and laser-induced damage of oxide coatings exposed to deep space radiation

Preliminary Characterization of Alumina-Forming Austenitic–Type Advanced Alloys as Structural Materials for LFRs