Abstract:Effects of atmosphere, temperatures and duration time on the surface topography and the electrical conductivity of LiNbO3 single crystals deposited with a 300-nm-thick layer of different metal films (Al, Mg and Zn) had been systematically investigated. LiNbO3 samples covered with Al film annealed at 500 degrees C for 6 h in different atmosphere were firstly studied. There were a lot of small holes generated after the residual film cleaning. In addition, the surface roughness was enhanced with increasing pressure. Compared with areas that without metal Al coated, a sharp step was formed, especially the deep step of about 125 nm in 3%H-2 + Ar atmosphere. The I-V curves reveal that the electrical conductivity of sample surface annealed at normal pressure was better than that in low vacuum. The current value was up to about 20 mA at 10 V in 3%H-2 + Ar, resulting in the conductivity significantly improved. Subsequently, samples deposited with different metal (Zn, Mg and Al, respectively) films annealed at 400 degrees C for 6 h in 3%H-2 + Ar were discussed. After wet etching, interestingly, a large number of nano sized protrusions were formed on the surface. Both of samples coated with Mg and Zn films presented no obvious step depth, while a clear step about 13 nm was formed for Al-coated samples. The I-V curves show that the surface conductivity of Zn-coated samples achieved the maximum of about 2.5 mA at 5 V among the three metals. Furthermore, Zn-coated samples annealed at different temperatures and holding time in 3%H-2 + Ar were also analyzed. After pickling, also, there were a lot of nanobulges appeared across the surface. With the temperatures keeping growth and the time extending, the nanobulges became much more compact and well-distributed. At the same time, the surface conductivity of samples would be gradually and effectively enhanced. The PL and XPS spectrums have indicated that more oxygen vacancies formed with increasing temperatures and holding time, resulting in the significant improvement in surface conductivity. The conduction mechanisms of sample surface can behave differently owing to the various annealing conditions.

Morphology of lithium niobium oxide thin film ultrasonic transducers deposited by RF magnetron sputtering

High-temperature thin film lithium niobium oxide transducers for bolts

Enhancement of piezoelectric response in V doped LiNbO3 films deposited by RF magnetron sputtering

Thinning of Lithium Niobate Wafers with a Novel Designed Lapping Tool and Measurements

Surface Morphology of LaNiO3thin Films and Its Dependence on Annealing Temperature

Effects of Atmosphere, Metal Films, Temperatures and Holding Time on the Surface Topography and Electrical Conductivity of LiNbO3 Single Crystals

Preparation and Study of Conductive LaNiO3 Thin Films on Different Substrates

Study on PZT/LaNiO3/MgO Heterostructures and Its Properties

Preparation and Characterization of LiNbO<sub>3</sub> Thin Films Derived from Metal Carboxylate Gels

Niobate-on-Niobate Resonators with Aluminum Electrodes

Characterization of Lithium Niobate Thin Films Derived from Aqueous Solution

Optical and Structural investigations of LiNbO3 thin films by PLD

Preparation and characterization of LiNbO3 thin films derived from metal carboxylate gels

Completely (001)-textured growth and electrical properties of Bi4Ti3O12/LaNiO3 heterostructures prepared by pulsed laser deposition on LaAlO3 single crystal substrates

Study on PZT /lanio_3/ LaAlO_3 Heterostructures and Its Properties

Omni‐functional crystal: Advanced methods to characterize the composition and homogeneity of lithium niobate melts and crystals

A Novel Morphology of High Voltage LiMn1.5Ni0.5O4 Cathode Material with Niobium-Doping

Ferroelectric domain inversion and its stability in lithium niobate thin film on insulator with different thicknesses

Preparation and performance of novel LLTO thin film electrolytes for thin film lithium batteries

In-situ Poling of Lithium Niobate Films on Silicon Wafer by Applying a Low Electric Field During Pulsed Laser Deposition