Anisotropic, biomorphic cellular Si3N4 ceramics with directional well-aligned nanowhisker arrays based on wood-mimetic architectures

Songsong Xu,Xiaonan Zhou,Qiang Zhi,Junjie Gao,Liucheng Hao,Zhongqi Shi,Bo Wang,Jianfeng Yang,Kozo Ishizaki

DOI: https://doi.org/10.1007/s40145-021-0555-1

IF: 11.534

2022-03-17

Journal of Advanced Ceramics

Abstract:Abstract Inspired by the transport behavior of water and ions through the aligned channels in trees, we demonstrate a facile, scalable approach for constructing biomorphic cellular Si 3 N 4 ceramic frameworks with well-aligned nanowhisker arrays on the surface of directionally aligned microchannel alignments. Through a facile Y(NO 3 ) 3 solution infiltration into wood-derived carbon preforms and subsequent heat treatment, we can faultlessly duplicate the anisotropic wood architectures into free-standing bulk porous Si 3 N 4 ceramics. Firstly, α-Si 3 N 4 microchannels were synthesized on the surface of C B -templates via carbothermal reduction nitridation (CRN). And then, homogeneous distributed Y−Si−O−N liquid phase on the walls of microchannel facilitated the anisotropic β-Si 3 N 4 grain growth to form nanowhisker arrays. The dense aligned microchannels with low-tortuosity enable excellent load carrying capacity and thermal conduction through the entire materials. As a result, the porous Si 3 N 4 ceramics exhibited an outstanding thermal conductivity (TC, k R ≈ 6.26 W·m −1 ·K −1 ), a superior flexural strength (σ L ≈ 29.4 MPa), and a relative high anisotropic ratio of TC ( k R / k L = 4.1). The orientation dependence of the microstructure-property relations may offer a promising perspective for the fabrication of multifunctional ceramics.

materials science, ceramics