Viscoelastic properties of copolycarbonates comprising isosorbide and 1,4-cyclohexanedimethanol

Ruiqi Han,Takumitsu Kida,Masayuki Yamaguchi
DOI: https://doi.org/10.1007/s00396-023-05143-9
2023-07-07
Abstract:Viscoelastic properties of copolycarbonate materials comprising isosorbide (ISB) and cyclohexanedimethanol (CHDM) were studied as a function of the ISB content. In the glassy state, β dispersion was clearly detected in the dynamic mechanical spectra. The tensile storage modulus E′ at room temperature increased with the ISB content, and the glass transition temperature T g , i.e., peak temperature of α dispersion, increased with the ISB content. It was found from oscillatory shear modulus that the rubbery plateau modulus G N 0 decreased with the ISB content. The entanglement molecular weights M e were found to be 2330–3640, which were slightly higher than that of bisphenol-A polycarbonate and much lower than those of poly(methyl methacrylate) and polystyrene. The onset shear stress of shark-skin failure at capillary extrusion was evaluated and found to increase with the ISB content.
polymer science,chemistry, physical
What problem does this paper attempt to address?