Abstract:Using CO2 polycarbonates as engineering thermoplastics has been limited by their mechanical performances, particularly their brittleness. Poly(cyclohexene carbonate) (PCHC) has a high tensile strength (40 MPa) but is very brittle (elongation at break <3%), which limits both its processing and applications. Here, well-defined, high molar mass CO2 terpolymers are prepared from cyclohexene oxide (CHO), cyclopentene oxide (CPO), and CO2 by using a Zn(II)Mg(II) catalyst. In the catalysis, CHO and CPO show reactivity ratios of 1.53 and 0.08 with CO2, respectively; as such, the terpolymers have gradient structures. The poly(cyclohexene carbonate)-grad-poly(cyclopentene carbonate) (PCHC-grad-PCPC) have high molar masses (86 < Mn < 164 kg mol-1, ĐM < 1.22) and good thermal stability (Td > 250 °C). All the polymers are amorphous with a single, high glass transition temperature (96 < Tg < 108 °C). The polymer entanglement molar masses, determined using dynamic mechanical analyses, range from 4 < Me < 23 kg mol-1 depending on the polymer composition (PCHC:PCPC). These polymers show superior mechanical performance to PCHC; specifically the lead material (PCHC0.28-grad-PCPC0.72) shows 25% greater tensile strength and 160% higher tensile toughness. These new plastics are recycled, using cycles of reprocessing by compression molding (150 °C, 1.2 ton m-2, 60 min), four times without any loss in mechanical properties. They are also efficiently chemically recycled to selectively yield the two epoxide monomers, CHO and CPO, as well as carbon dioxide, with high activity (TOF = 270-1653 h-1, 140 °C, 120 min). The isolated recycled monomers are repolymerized to form thermoplastic showing the same material properties. The findings highlight the benefits of the terpolymer strategy to deliver thermoplastics combining the beneficial low entanglement molar mass, high glass transition temperatures, and tensile strengths; PCHC properties are significantly improved by incorporating small quantities (23 mol %) of cyclopentene carbonate linkages. The general strategy of designing terpolymers to include chain segments of low entanglement molar mass may help to toughen other brittle and renewably sourced plastics.

Stereoregular Poly(Cyclohexene Carbonate)S: Unique Crystallization Behavior

Stereoregular polycarbonate synthesis: Alternating copolymerization of CO <sub>2</sub> with aliphatic terminal epoxides catalyzed by multichiral cobalt(III) complexes

Stereoregular polycarbonate synthesis: Alternating copolymerization of CO2 with aliphatic terminal epoxides catalyzed by multichiral cobalt(III) complexes

Enhanced Asymmetric Induction for the Copolymerization of CO2 and Cyclohexene Oxide with Unsymmetric Enantiopure SalenCo(III) Complexes: Synthesis of Crystalline CO2-Based Polycarbonate

Highly Selective Synthesis Of Co2 Copolymer From Styrene Oxide

Crystalline CO2 copolymer from epichlorohydrin via Co(III)-complex-mediated stereospecific polymerization

Isomorphic crystallization of aliphatic copolyesters derived from 1,6-hexanediol: Effect of the chemical structure of comonomer units on the extent of cocrystallization

A Bifunctional Β-Diiminate Zinc Catalyst with CO2/Epoxides Copolymerization and RAFT Polymerization Capacities for Versatile Block Copolymers Construction

Pinwheel-Shaped Tetranuclear Organoboron Catalysts for Perfectly Alternating Copolymerization of CO2 and Epichlorohydrin.

Study of Preparation and Properties of Stereoregular Poly(cyclohexenylene carbonate)

Cobalt(III)‐complex‐mediated Terpolymerization of CO2, Styrene Oxide, and Epoxides with an Electron‐donating Group

Triethyl Borane-Regulated Selective Production of Polycarbonates and Cyclic Carbonates for the Coupling Reaction of CO2 with Epoxides

Unveiling Chain–chain Interactions in CO 2 -Based Crystalline Stereocomplexed Polycarbonates by Solid-State NMR Spectroscopy and DFT Calculations

Crystallization Behavior and Morphology of Novel Aliphatic Poly (Monothiocarbonate)s

Multifunctional Linear And Hyperbranched Five-Membered Cyclic Carbonate-Based Polymers Directly Generated From Co2 And Alkyne-Based Three-Component Polymerization

Regioselective and Alternating Copolymerization of Carbonyl Sulfide with Racemic Propylene Oxide

Solution Crystallization Behavior Of Crystalline-Crystalline Dibloek Copolymers Of Poly(Ethylene Oxide)-Block-Poly(Epsilon-Caprolactone)

Studies on synthesis and optical properties of poly(isosorbide-co-1,4-cyclohexanedimethanol) carbonate

Crystallization and Morphology of Star-Shaped Polyethylenoxyde- B -Polycaprolactone under High Pressure Carbon Dioxide

Organic-Inorganic Hybrid Materials: Tailoring Carbon Dioxide-Based Polycarbonate with POSS-SH Crosslinking

Controlled Carbon Dioxide Terpolymerizations to Deliver Toughened yet Recyclable Thermoplastics