The Effect Of Diisocyanate Isomer Composition On Optical And Adhesive Properties Of Polyurethanes Based On 4,4 '-Dicyclohexyl Methane Diisocyanate

Hou Junxian,Li Lei,Liu Weidong,Yan Yue,Chen Xiangbao

2010-01-01

Abstract:Polyurethanes wereprepared having 47 wt % hard segments based on 4,4'-dicyclohexyl methane diisocyanate (H-12 MDI) with trans. trans isomer contents in the 16 to 99 mol % range and 1,4-butanediol chain extender. The soft segments is polytetramethylene glycol (PTMEG, Mw 1000). H-12 MDI with 25, 40, 60, 80 and 99% trans,trans isomer contents were obtained from commercial H-12 MDI (16% trans, trans) by fractional crystallization, and all polyurethanes were prepared by a two-step bulk polymerization procedure. The polyurethanes based on H-12 MDI with trans,trans contents of 40% or higher yielded materials insoluable in N,N-dimethylformaide (DMF) and were generally opaque. Mechanical properties, such as tensile strength at break, decreased with increasing trans,trans content, while the Young's modulus and Shore hardness increased. A decrease in adhesion strength is produced when content of t, t-H-12 MDI is above 25%. Wide-angle and small-angle X-ray scattering at room temperature were employed to characterize phase morphology. The mean macrolattice spacings between stiff fragments (STF) decreased in the order t, t-H-12 MDI-0. 16 > t, t-H-12 MDI-0. 25 > t, t-H-12 MDI-0. 40 > t, t-H-12 MDI-0. 60 > t, t-H-12 MDI-0. 80 > t, t-H-12 MDI-0. 99.