Abstract:Terahertz (THz) non-destructive testing can detect internal defects in dielectric materials. However, this technology is mainly used for detecting thin and simple structures at present, lacking validations for the detection effectiveness of internal defects in thicker and more complex structures, such as fiber-web-reinforced composite sandwich panels. In this study, samples of fiber-web-reinforced polymethacrylimide foam sandwich panels, which are, respectively, 20 mm and 30 mm thick, were made to detect the internal debonding, inclusion, pore, and crack defects by the THz time-domain spectroscopy system (THz-TDS). The peak-to-peak-imaging algorithm, maximum-amplitude-imaging algorithm, minimum-amplitude-imaging algorithm, pulse-width-imaging algorithm, and time-of-flight-imaging algorithm were used to process and image the collected THz signals. The results showed that the peak-to-peak-imaging algorithm had the best performance. To address the low imaging resolution of THz-TDS, a block-based super-resolution reconstruction method—SSSRGAN—is proposed, which can improve image resolution while maintaining the clear edge contours of defects. The defect-detection results of the samples showed that THz-TDS could detect all pore, debonding, and crack defects, with a minimum size of 3 mm for pores and debonding and a minimum thickness of 1 mm for cracks. The method showed poor detection performance for inclusions with a thickness of 0.053 mm, but could still extract the defect features. Based on the THz-TDS reflection mode measurement principle, the thickness information of the panel, foam core, and web of the samples was calculated: the measurement error was no more than 0.870 mm for Sample #1 and no more than 0.270 mm for Sample #2, demonstrating the accuracy of THz-TDS in measuring the dimensions of sandwich panel structures. In general, THz technology shows potential for detecting internal defects and performing dimensional measurements in complex structures. With the advancement of portable devices and enhancements in detection speed, real-time on-site detection is anticipated in the future.

LFM-Chirp-Square pulse-compression thermography for debonding defects detection in honeycomb sandwich composites based on THD-processing technique

Debonds and Water-Filled Defects Detection in Honeycomb Sandwich Composites Based on Pulse Infrared Thermography NDT Technique

Research on Internal Defect Detection of Epoxy Glass Fiber Composites Based on Terahertz Imaging Technology

Study on debonding defects detection of CFRP / Al honeycomb structure by Square-wave thermography

Inspection of defects in composite structures using long pulse thermography and shearography

Defect detection of GFRP/Nomex honeycomb sandwich structure by linear frequency modulation infrared thermal imaging

Health monitoring of the composite honeycomb insulation panels using thermographic image processing

Research on pulse infrared thermal wave detection technology for honeycomb sandwich structure defects

Terahertz Nondestructive Testing of Honeycomb Composites Based on FMCW Technology

Low-velocity Impact Damage Detection in CFRP Composites by Applying Long Pulsed Thermography Based on Post-Processing Techniques

An Improved Damage Index for Non-Destructive Testing of a Honeycomb Sandwich Panel Using Guided Waves

Halogen Optical Referred Pulse-Compression Thermography for Defect Detection of CFRP

Measurement Methodology: Terahertz Technique: A Non-Destructive Testing Method for Composite Defect Detection

Identifying Defects in Aerospace Composite Sandwich Panels Using High-Definition Distributed Optical Fibre Sensors

Non-Destructive Testing of a Fiber-Web-Reinforced Polymethacrylimide Foam Sandwich Panel with Terahertz Time-Domain Spectroscopy

Nondestructive Inspection and Quantification of Select Interface Defects in Honeycomb Sandwich Panels

Convolution Neural Network Fusion High Power Halogen Lamp Induced Thermal-Wave Diffusion Multidimensional Features: an Intelligent Defect Identification Approach for Aviation Honeycomb Sandwich Composites

Multi-frequency Fused Lock-in Thermography in Detecting Defects at Different Depths

Defect Detection in Aerospace Sandwich Composite Panels Using Conductive Thermography and Contact Sensors

Thermographic inspection of water ingress in composite honeycomb sandwich structure: a quantitative comparison among Lock-in thermography algorithms

Numerical and experimental investigation on debonding detection in honeycomb sandwich using air-coupled local defect resonance and coda wave analysis