Abstract:Terahertz (THz) non-destructive testing can detect internal defects in dielectric materials. However, this technology is mainly used for detecting thin and simple structures at present, lacking validations for the detection effectiveness of internal defects in thicker and more complex structures, such as fiber-web-reinforced composite sandwich panels. In this study, samples of fiber-web-reinforced polymethacrylimide foam sandwich panels, which are, respectively, 20 mm and 30 mm thick, were made to detect the internal debonding, inclusion, pore, and crack defects by the THz time-domain spectroscopy system (THz-TDS). The peak-to-peak-imaging algorithm, maximum-amplitude-imaging algorithm, minimum-amplitude-imaging algorithm, pulse-width-imaging algorithm, and time-of-flight-imaging algorithm were used to process and image the collected THz signals. The results showed that the peak-to-peak-imaging algorithm had the best performance. To address the low imaging resolution of THz-TDS, a block-based super-resolution reconstruction method—SSSRGAN—is proposed, which can improve image resolution while maintaining the clear edge contours of defects. The defect-detection results of the samples showed that THz-TDS could detect all pore, debonding, and crack defects, with a minimum size of 3 mm for pores and debonding and a minimum thickness of 1 mm for cracks. The method showed poor detection performance for inclusions with a thickness of 0.053 mm, but could still extract the defect features. Based on the THz-TDS reflection mode measurement principle, the thickness information of the panel, foam core, and web of the samples was calculated: the measurement error was no more than 0.870 mm for Sample #1 and no more than 0.270 mm for Sample #2, demonstrating the accuracy of THz-TDS in measuring the dimensions of sandwich panel structures. In general, THz technology shows potential for detecting internal defects and performing dimensional measurements in complex structures. With the advancement of portable devices and enhancements in detection speed, real-time on-site detection is anticipated in the future.

Measurement Methodology: Terahertz Technique: A Non-Destructive Testing Method for Composite Defect Detection

Research on Internal Defect Detection of Epoxy Glass Fiber Composites Based on Terahertz Imaging Technology

A Nonlinear Method for Characterizing Discrete Defects in Thick Multilayer Composites

Identifying Delamination in Carbon Fiber Composites Based on Defect Modes in Imperfect Phononic Crystals

Ultrasonic Detection Method of Micro Defects in Thick-Section CFRP

Non-Destructive Testing of a Fiber-Web-Reinforced Polymethacrylimide Foam Sandwich Panel with Terahertz Time-Domain Spectroscopy

Inspection of defects in composite structures using long pulse thermography and shearography

Nondestructive Testing and Predictability of Microcracks in Carbon Fiber-Reinforced Composites via Terahertz Time-Domain Spectroscopy

Nondestructive Testing of Defects in Polymer–Matrix Composite Materials for Marine Applications Using Terahertz Waves

Terahertz time-domain spectroscopy for the inspection of dry fibre preforms

Quantitative non-destructive evaluation of CFRP delamination defect using laser induced chirp-pulsed radar photothermal tomography

Nondestructive testing and evaluation techniques of defects in fiber-reinforced polymer composites: A review

Thickness Measurement of Composite Material Using Eddy Current Testing

Terahertz Nondestructive Testing of Honeycomb Composites Based on FMCW Technology

Ultrasonic Phased Array Imaging Approach Using Omni-Directional Velocity Correction for Quantitative Evaluation of Delamination in Composite Structure

Nondestructive testing of bonding defects in multilayered ceramic matrix composites using THz time domain spectroscopy and imaging

High Precision Detection Method for Delamination Defects in Carbon Fiber Composite Laminates Based on Ultrasonic Technique and Signal Correlation Algorithm

LFM-Chirp-Square pulse-compression thermography for debonding defects detection in honeycomb sandwich composites based on THD-processing technique

Detection and identification of delamination defects in CFRP laminates using nonlinear frequency-modulated infrared thermal wave testing technology

Non-destructive testing and structural health monitoring technologies for carbon fiber reinforced polymers: a review

Non-destructive testing and evaluation of composite materials/structures: A state-of-the-art review