Abstract:alpha-Alumina (alpha-Al2O3), widely used as a raw material or production in advanced manufacturing industry, has attracted much attention in terms of its preparation temperature. A simple dissolution-evaporation-precipitation process was employed to obtain the amorphous Al-oxalate (AAO) precursor, serving as the starting material for the low temperature preparation of nano alpha-Al2O3. The crystalline structure and thermal behavior of the AAO were compared with commercially available aluminum hydroxide (Al(OH)(3)) powder using the X-ray powder diffraction (XRD) instrument, the thermal gravity analysis and differential scanning calorimetry (TG-DSC). The phase transition mechanism of AAO was investigated by the fourier transform infrared spectroscopy (FTIR), transmission electron microscope (TEM), scanning electron microscope (SEM), and Al-27 magic angle spinning nuclear magnetic resonance (Al-27-MAS-NMR). The DSC results indicated that AAO underwent a phase transformation at 982 degrees C. The alpha-alumina diffraction peaks appeared in AAO at 1000 degrees C, while alpha-Al2O3 phase was observed for Al(OH)(3) at 1200 degrees C. Furthermore, an absorption peak at 452 cm(-1), corresponding to Al-O bond in alpha-alumina was detected at 1000 degrees C. The proposed low-temperature preparation mechanism of alpha-alumina from AAO is as follows: four coordination Al-oxalate species entities coexist within the AAO sample; with increasing temperature, organic acid functional groups oxidize and volatilize, resulting in the formation of tetra-coordinate [AlO4], penta-coordinate [AlO5], and hexa-coordinate [AlO6] atomic groups; these atomic clusters further polymerize to form a structurally dense alpha-alumina crystal at the nano-scale (similar to 50 nm) at around 1000 degrees C. The experimental findings present a novel approach and method for the low-temperature preparation of nano-sized alumina powder. Additionally, a feasible theoretical reference for the low-temperature phase transition mechanism of amorphous Al-oxalate was provided.

Low-temperature synthesis of α-Al2O3 single crystal platelets by one-step thermal decomposition of Al-urea complex

Novel temperature dependent process for α-Al2O3 platelets

Low Temperature Phase Transition Mechanism of Amorphous Al-oxalate to Nano Α-Alumina

Low-Temperature Fabrication of Plate-like α-Al2O3 with Less NH4F Additive

Study of the Synthesis of Α-Al_2o_3 Platelet Crystal by Anhydrous Potassium Alum with the Molten Salt Method

Co‐templating Ionothermal Synthesis and Crystal Structure of a New Layered Aluminophosphate from a Protic Deep Eutectic Solvent

Synthesis of thin alpha alumina platelets with a large aspect ratio

Facile synthesis of nano-crystalline alpha-alumina at low temperature via an absolute ethanol sol-gel strategy

Preparation of α-Al2O3 by low-temperature calcining γ-Al2O3 with α-phase seed in-situ obtained by ball milling

Low-Temperature Synthesis and Characterization of AlPO-Cristobalite in Ionic Liquid

Facile synthesis of monodisperse aluminum nitride microspheres

Synthesis of plate-like α-Al2O3 single-crystal particles in NaCl–KCl flux using Al(OH)3 powders as starting materials

Low-Temperature Synthesis of Highly Dispersed Calcium Aluminate

Preparation and Characterization of Α-Al2o3 Film by Low Temperature Thermal Oxidation of Al8Cr5 Coating

Preparation of alumina ceramic template by the molten salt method

Synthesis of α-Al2O3 Nanopowders at Low Temperature from Aluminum Formate by Combustion Process

Lowering the synthesis temperature of α‐Al2O3 by increasing the content of pentacoordinate aluminum in the precursors

Low-temperature synthesis of high quality Ni-Fe layered double hydroxides hexagonal platelets

Synthesis of Aluminum Nitride Nanocrystals and Platelets

Low-temperature preparation of α-Al2O3 with the assistance of seeding a novel hydroxyl aluminum oxalate

Hydrothermal Synthesis of Magnesium Aluminate Platelets