Abstract:Facile synthesis of nano-crystalline alpha-Al2O3 at low temperature was systematically investigated. An easily accessible and reproducible sol-gel strategy utilizing aluminum isopropoxide, absolute ethanol and nitric acid (or hydrochloric acid) as raw materials was designed. The thermal decomposition of the precursor (gel) and subsequent formation of alpha-Al2O3 were characterized by X-ray diffraction (XRD), nitrogen adsorption and desorption measurements, thermogravimetric-differential scanning calorimetry (TG-DSC) and Fourier transform infrared spectra (FTIR). During the process of subsequent low temperature heat treatment of precursor gel, the formation of alpha-Al2O3 was firstly observed at temperature as low as 400 degrees C without the appearance of other transition phases. However, the additional gamma-Al2O3 diffraction peaks appeared at 800 degrees C unexpectedly and then gradually disappeared in the further calcination stage up to 1000 degrees C. These phenomena could not be illustrated by the traditional alumina phase transformation theories. Herein, a hypothetical scheme was put forward to explain these unique phenomena met with in our investigation. Besides, the critical role of the acid modifier in lowering the phase transformation temperature of alpha-Al2O3 was also carefully studied. The results indicated that the increasing molar ratio of acid to aluminum isopropoxide and using nitric acid as modifier were in favor of the phase transformation from gamma- to alpha-Al2O3. (C) 2012 Elsevier B.V. All rights reserved.

Low-temperature preparation of α-Al2O3 with the assistance of seeding a novel hydroxyl aluminum oxalate

Preparation of α-Al2O3 by low-temperature calcining γ-Al2O3 with α-phase seed in-situ obtained by ball milling

Lowering the synthesis temperature of α‐Al2O3 by increasing the content of pentacoordinate aluminum in the precursors

Preparation of spherical α‐Al 2 O 3 nanoparticles by microwave hydrothermal synthesis and addition of nano‐Al seeds

Preparation of Near-Spherical α-Al2O3 Particles by Enhanced Precipitation of Gibbsite from Sodium Aluminate Solution Using Highly Dispersed Al2O3 as Seeds

Preparation of Self-Healing Α-Al2o3 Films by Low Temperature Thermal Oxidation

Facile synthesis of nano-crystalline alpha-alumina at low temperature via an absolute ethanol sol-gel strategy

Preparation of Near-Spherical α-Al 2 O 3 Particles by Enhanced Precipitation of Gibbsite from Sodium Aluminate Solution Using Highly Dispersed Al 2 O 3 as Seeds

A novel low temperature synthesis technique of sol–gel derived nanocrystalline alumina abrasive

Synthesis and phase formation mechanism of alpha-Fe2O3 powders by hydrothermal reaction method

Low-Temperature Fabrication of Plate-like α-Al2O3 with Less NH4F Additive

Study on ultrasound-assisted preparation of sphere-like high-purity alumina

Preparation and Characterization of Α-Al2o3 Film by Low Temperature Thermal Oxidation of Al8Cr5 Coating

Enhanced Formation of Α-Al2o3 at Low Temperature on Cr/Al Coating by Controlling Oxygen Partial Pressure

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Preparation of High Purity Alumina Ceramic Supports at Low Temperature

Fabrication of Α-Alo(oh)·sio2 with Core-Shell Structures by Heterogeneous Nucleation-and-growth Processing

Production of ultrafine alpha alumina powders and fabrication of fine grained strong ceramics

Preparation of Self-Coating Al2O3 Bonded SiAlON Porous Ceramics Using Aluminum Dross and Silicon Solid Waste under Ambient Air Atmosphere

Synthesis of α-Al2O3 Nanopowders at Low Temperature from Aluminum Formate by Combustion Process

Preparation of Fineα-Al_2O_3 Powders by Calcining Carbon-coveredγ-Al_2O_3 in Oxygen