Abstract:alpha-Al2O3 is one of the most promising hydrogen permeation barriers due to its high melting point, stable chemical properties, and good machinability. However, alpha-Al2O3 synthesis usually requires temperatures above 1200 degrees C, which weakens the properties of the substrate material. Therefore, low-temperature preparation of alpha-Al2O3 is crucial. Most studies have reported that using Cr2O3 as a template is a good method to promote alpha-Al2O3 formation. However, the formation of monolithic Cr2O3 is still a challenge. To address these problems, a Cr/Al coating was introduced that was successfully deposited on stainless steel. A new composite coating was formed by the subsequent oxidation conversion under ultra-low-partial-pressure conditions via decomposing the oxygen precursors (nickel/iron oxide) in a closed environment. The results from X-ray diffraction, Raman spectra and other methods showed that the content of alpha-Al2O3 was enhanced at 2.6 x 10(-24) Pa (theoretical calculation value) and promoted the formation of near-stoichiometric Cr2O3. In addition, the ultra-low partial pressure condition could promote the diffusion of defects on the interface between metastable Al2O3 and corundum crystal structure Cr2O3, by which the alpha-Al2O3 was successfully formed at 600 degrees C due to the template effect of Cr2O3. This work provides a new approach for the low-temperature preparation of alpha-Al2O3.

Preparation and Characterization of Α-Al2o3 Film by Low Temperature Thermal Oxidation of Al8Cr5 Coating

Preparation of Self-Healing Α-Al2o3 Films by Low Temperature Thermal Oxidation

Preparation of Self-Healing Α-Al2o3 Film on Rapid Quenching Al-Cr Alloy by Thermal Oxidation at Low Temperature

Al-Cr Coatings Prepared by Diffusion at Low Temperature and Its Phase Characterization

Surface Characterization of Thermally Oxidized Titanium Alloys

Enhanced Formation of Α-Al2o3 at Low Temperature on Cr/Al Coating by Controlling Oxygen Partial Pressure

Preparation of Al-Cr-Fe Coatings by Heat Treatment of Electrodeposited Cr/Al Composite Coatings

Analysis on behaviors of contact reaction between quenched Al-Cr foils and stainless steel

Preparation and Characterization of Al11cr4 Phase by Diffusion of Al/Cr Composite Film

Effects of Heat Treatment on Structure Transformation of Cr/Al Composite Coatings

Observation on the Interface of Α-Al2o3/cr2o3: Prepared by Oxidation of Al45Cr7

High Temperature Oxidation Behaviors of Al/Cr Composite Coating on Ti2AlNb Alloy

Formation of aluminide coatings by low-temperature heat treatment of Al coating electrodeposited from ionic liquid

EFFECT OF MCrAlY COATINGS ON OXIDATION RESISTANCE OF TiAl INTERMETALLICS

Oxidation Behaviour of Sputter-Depositedni–cr–al Micro-Crystalline Coatings

High-temperature steam oxidation behavior and failure mechanisms of Al alloyed Cr coatings on Zr-4 alloy

Effects of Chromium on the Oxidation Performance of β-FeAlCr Coatings

Oxidation Behaviour of Β-Fealcr Coating Produced by Close-Field Unbalanced Magnetron Sputter Deposition

Microstructure evolution and high temperature air oxidation behaviour of thick Cr coatings at 1200°C

Improving the high temperature oxidation resistance of TiAl alloy by SiOC coating

High-Temperature Oxidation And Tensile Behaviors Of Cral Coating On Zirconium Alloy