Abstract:Amorphous alumina films are isotropic and have no grain boundaries, which make them have smooth surfaces, excellent properties, and wide applications in protective coatings, catalysis, and microelectronics. However, high-quality alumina films were usually prepared by vapor-phase approaches which need expensive equipment and long production time. Additionally, amorphous films are long-range disordered, which makes the study of structure–property relationships challenging. Here, a simple sol–gel method is employed to obtain high-quality amorphous Al2O3 thin films. The microstructure, morphology, and mechanical properties of amorphous Al2O3 thin films were systematically investigated. All the Al2O3 thin films heat-treated at 600–800∘C are in amorphous state with ultrasmooth surface (Ra values about 0.29–0.43 nm) and high mechanical properties (elastic modulus ∼170[Formula: see text]GPa, hardness ∼20[Formula: see text]GPa). The mechanical properties (E and H) of Al2O3 films gradually increase with the increase of heat-treating temperature. Additionally, the Al coordination of the amorphous alumina films are analyzed by solid-state NMR and correlated with the mechanical properties. The results show that in amorphous alumina, the presence of tetrahedral Al ([4]Al) and octahedral Al ([6]Al) is helpful to improve the mechanical properties, while the five-coordinated Al ([5]Al) is not conducive to improve the mechanical properties. The results demonstrate that sol–gel method is an attractive alternative to time-consuming and expensive vapor-phase approaches and are useful for scale-up to applications and research of amorphous alumina films.

Morphology-controlled Synthesis of Α-Alumina Microplatelets Through an Additive-Assisted Molten Salt Reaction

Synthesis of thin alpha alumina platelets with a large aspect ratio

Preparation of alumina ceramic template by the molten salt method

Silica Nanoparticle-Decorated Alumina Rough Platelets for Effective Reinforcement of Epoxy and Hierarchical Carbon Fiber/epoxy Composites

Size Control of α-Al<sub>2</sub>O<sub>3</sub>Platelets Synthesized in Molten Na<sub>2</sub>SO<sub>4</sub>Flux

Novel temperature dependent process for α-Al2O3 platelets

Aluminium induced sub-microsized α-Al2O3 platelets in the soda-lime-silica glass

Size control of α-Al2O3 platelets synthesized in molten Na2SO4 flux

Aluminium Induced Sub-Microsized <i>α</i>-Al<sub>2</sub>O<sub>3</sub> Platelets in the Soda-Lime-Silica Glass

Preparation of platelet CaMg2Al16O27 (CM2A8) grains via adjusting MgO and Al2O3 contents

The Microstructure, Morphology, and Mechanical Properties of Sol-Gel-derived Amorphous Aluminum Oxide Films

Study of the Synthesis of Α-Al_2o_3 Platelet Crystal by Anhydrous Potassium Alum with the Molten Salt Method

Synthesis and properties of high aspect ratio SrBi 4 Ti 4 O 15 microplatelets

Effect of Synthesizing Temperature of Alumina Powder with Rose-Like Structure on the Microstructure and Mechanical Property of Alumina Ceramic

α-Calcium Sulfate Hemihydrate Nanorods Synthesis: A Method for Nanoparticle Preparation by Mesocrystallization

Morphology Controllable Synthesis Of Gamma-Alumina Nanostructures Via An Ionic Liquid-Assisted Hydrothermal Route

Morphological Controlled Growth of Nanosized Boehmite with Enhanced Aspect Ratios in an Organic Additive-Free Cationic–Anionic Double Hydrolysis Method

Influence of starting materials on plate-like alumina synthesized by molten salt method

Size and Morphology Controlled Synthesis of Boehmite Nanoplates and Crystal Growth Mechanisms

Influence of SiO2 addition on the sintering behavior and kinetics of fine-sized α-Al2O3 nanoparticles

Size-controlled synthesis of nano α-alumina particles through the sol–gel method