Abstract:Additive manufacturing (AM) introduces unique grain feature and anisotropy in metals, as well as relatively poor surface quality, so the knowledge about the formation of post-machining-induced surface integrity needs to be extended. This study aims to understand the machining phenomena in orthogonal cutting of Inconel 718 produced via powder bed fusion of metals using a laser beam system (PBF-LB/M), paying particular attention to the cutting energy, chip formation, geometrical defects, and microstructural deformation. Experiments are conducted on both wrought (W 718) and PBF-LB/M (PBF 718) Inconel 718, whereby the cutting speed and the anisotropy of the workpiece in the raw state play an important role. The results indicate that less cutting energy is consumed when cutting PBF 718 in the direction perpendicular to its build direction (BD), followed by cutting in its BD. Denser shearing-induced slip lines and relatively continuous chip morphology are found when cutting PBF 718 in its BD, moreover, the effect of cutting speed on shearing deformation of columnar grains under this condition is analysed. More importantly, this study identifies a significant geometrical defect phenomenon which is unique to PBF 718 and highly depends on the cutting speed and anisotropy of grain feature. A detailed characterisation shows that this behaviour is caused by tearing within the grains in the matrix material and not by the presence of hard inclusions, which has rarely been reported in the literature. The microstructure in the subsurface area exhibits that the density of grain boundaries in the cutting direction plays the key role in plastic deformation, as the machining process mainly causes dragging behaviour in the area below the machined surface. Thus, cutting PBF 718 in the direction perpendicular to its BD shows similar deformation layer to W 718, while cutting PBF 718 in its BD displays much stronger subsurface deformation. The obtained results greatly help to understand the cutting phenomena in post-machining of additively manufactured Ni-based components, especially the integrity for a better functional surface.

An Experimentally Informed Computational Framework for Investigating the Role of Surface Roughness on High Cycle Fatigue Life of LPBF IN718

Effect of Surface Modification on the High Temperature Low Cycle Fatigue Performance of LPBF 316L Austenitic Steel

An Approach to Estimate the Low Cycle Fatigue Probabilistic Curves of PBF-LB/M 316L Steel from Small Size Datasets Using the Remora Optimization Algorithm

Surface roughness-informed fatigue life prediction of L-PBF Hastelloy X at elevated temperature

Microstructural, mechanical and wear behaviour of Inconel-718 produced through laser-powder bed-fused additive manufacturing

Surface condition driven fatigue performance of laser powder bed fusion H13 steel

Impact of Surface and Pore Characteristics on Fatigue Life of Laser Powder Bed Fusion Ti-6Al-4V Alloy Described by Neural Network Models

Role of defects and microstructure on the fatigue durability of Inconel 718 obtained by additive layer manufacturing route

Influence of post-processing on very high cycle fatigue resistance of Inconel 718 obtained with laser powder bed fusion

Development of an efficient multi-scale model to predict residual stresses and distortions in the laser powder bed fusion process for Inconel-718

Influence of LPBF-Surface Characteristics on Fatigue Properties of Scalmalloy®

Electrical Current-Assisted Low-Plasticity Burnishing of Inconel 718 Built by Laser Powder Bed Fusion: Surface Integrity and Fatigue Life Analysis

The Use of Miniature Specimens to Determine Local Properties and Fracture Behavior of LPBF-Processed Inconel 718 in as-Deposited and Post-Treated States

Correlation between Surface Integrity and Low Cycle Fatigue Life of Machined Inconel 718

On machining-induced surface integrity of Inconel 718 fabricated by powder bed fusion

Study on the Effect of Powder-Bed Fusion Process Parameters on the Quality of as-Built IN718 Parts Using Response Surface Methodology

Surface Treatment of Powder-Bed Fusion Additive Manufactured Metals for Improved Fatigue Life

Effects of Sandblasting and HIP on Very High Cycle Fatigue Performance of SLM-fabricated IN718 Superalloy

Optimization of electric current-assisted sustainable burnishing process of additively manufactured Inconel 718: trade-off between production rate and fatigue life

Experimental investigation of process parameter variations on the microstructure and failure behavior of IN718 structures in PBF-LB/M

High Cycle Fatigue Behavior of 316L Steel Fabricated by Laser Powder Bed Fusion: Effects of Surface Defect and Loading Mode