Experimental investigation of process parameter variations on the microstructure and failure behavior of IN718 structures in PBF-LB/M

Hannes Panzer,Johannes Diller,Fabian Ehrenfels,Jonathan Brandt,Michael F. Zäh

DOI: https://doi.org/10.2351/7.0001232

IF: 2.1

2024-01-02

Journal of Laser Applications

Abstract:Conventional manufacturing technologies, such as milling or casting, are limited in terms of the manufacturable complexity of the parts to be produced. They are also restricted in terms of the local modifiability of the mechanical properties. Additive manufacturing, specifically the Powder Bed Fusion of Metals using a Laser Beam (PBF-LB/M), is a novel method, which is capable of addressing both limitations. However, the resulting parts are often prone to cracking during PBF-LB/M and in the service afterward because of high thermally induced local stress intensities. Selectively modifying the process parameters during the fabrication can be a suitable strategy to locally reduce the failure susceptibility. Over the course of this study, samples made from the nickel-based superalloy Inconel 718 were manufactured with varying laser powers, hatch distances, and scan speeds. The samples were divided into stress crack specimens as well as static and dynamic tensile test specimens. The grain structure was investigated, and correlations between the microstructure and the cracking susceptibility were determined. It was found out that variations in the laser power had the most pronounced effect on the grain structure and the failure behavior. An increasing grain size enhanced the fracture resistance in the stress crack samples while the static and dynamic mechanical properties deteriorated. Based on these results, the application area of PBF-LB/M could potentially be widened due to the manufacturability of parts otherwise susceptible to stress-induced cracking. The mechanical properties of as-built parts can remain unchanged utilizing a local process parameter adaption.

materials science, multidisciplinary,optics,physics, applied

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to improve the microstructure and crack - resistance performance of Inconel 718 structural parts fabricated by powder - bed laser melting (PBF - LB/M) through adjusting process parameters. Specifically, the paper investigates how the changes in laser power, hatch distance and scanning speed affect the microstructure of the material and its crack behavior under stress - induction. The main objectives of the study include:

1. **Evaluating the adjustability of stress - induced cracks**: Explore whether stress - induced cracks in Inconel 718 fabricated by PBF - LB/M can be changed by adjusting the microstructure.
2. **Determining the key process parameters**: Identify which of the laser power, hatch distance and scanning speed has the most significant impact on the microstructure and failure behavior.
3. **Establishing the relationship between VED and microstructure and crack sensitivity**: Verify the correlation between volume energy density (VED) and the final microstructure and crack sensitivity.
4. **Analyzing the influence of crack size reduction parameters on static and dynamic mechanical properties**: Study how the parameters for reducing crack size affect the static and dynamic mechanical properties of the material.

Through these studies, the author hopes to broaden the application range of PBF - LB/M technology, especially when manufacturing components prone to stress - induced cracks, being able to maintain or improve mechanical properties by locally adjusting process parameters.