Abstract:Additive manufacturing, especially laser powder bed fusion (L-PBF), is widely used for fabricating metal parts with intricate geometries. However, parts produced via L-PBF suffer from varied surface roughness which affects the dynamic or fatigue properties. Accurate prediction of fatigue properties as a function of surface roughness is a critical requirement for qualifying L-PBF parts. In this work, an analytical methodology is put forth to predict the fatigue life of L-PBF components having heterogeneous surface roughness. Thirty-six Hastelloy X specimens are printed using L-PBF followed by industry-standard heat treatment procedures. Half of these specimens are built with as-printed gauge sections and the other half is printed as cylinders from which fatigue specimens are extracted via machining. Specimens are printed in a vertical orientation and an orientation 30 degree from the vertical axis. The surface roughness of the specimens is measured using computed tomography and parameters such as the maximum valley depth are used to build an extreme value distribution. Fatigue testing is conducted at an isothermal condition of 500-degree F. It is observed that the rough specimens fail much earlier compared to the machined specimens due to the deep valleys present on the surfaces of the former ones. The valleys act as notches leading to high strain localization. Following this observation, a functional relationship is formulated analytically that considers surface valleys as notches and correlates the strain localization around those notches with fatigue life, using the Coffin-Manson-Basquin and Ramberg-Osgood equation. In conclusion, the proposed analytical model successfully predicts the fatigue life of L-PBF specimens at an elevated temperature undergoing different strain loadings.

What problem does this paper attempt to address?

The paper attempts to address the issue of fatigue life prediction for Hastelloy X manufactured by Laser Powder Bed Fusion (L-PBF) under high temperatures due to uneven surface roughness. Specifically, the study aims to develop an analytical method to predict the fatigue life of L-PBF components based on their surface roughness under high-temperature conditions. ### Background and Motivation - **Background**: Additive manufacturing technology, especially L-PBF, is widely used for producing metal components with complex geometries. However, the uneven surface roughness of L-PBF manufactured parts affects their dynamic or fatigue performance. - **Problem**: Accurately predicting the relationship between fatigue performance and surface roughness is crucial for the qualification of L-PBF components. Existing studies on the fatigue behavior of Hastelloy X manufactured by L-PBF under high temperatures are limited, and current predictive models mainly focus on high-cycle fatigue life, with poor performance in predicting low-cycle fatigue life. ### Research Objectives - **Objective**: To propose an analytical method to predict the fatigue life of Hastelloy X components manufactured by L-PBF based on their surface roughness under high-temperature conditions. - **Specific Questions**: - How to quantify the surface roughness of Hastelloy X components manufactured by L-PBF? - How does surface roughness affect the fatigue life of these components under high-temperature conditions? - How to establish a model that can accurately predict fatigue life? ### Method Overview - **Experimental Design**: 36 Hastelloy X samples were prepared, with half retaining the as-printed surface state (rough) and the other half undergoing mechanical surface treatment (smooth). The samples were printed at vertical and 30° inclined angles. - **Surface Roughness Measurement**: Surface roughness parameters, such as maximum valley depth, were measured using computed tomography (CT) and extreme value distributions were constructed. - **Fatigue Testing**: Fatigue tests were conducted under isothermal conditions at 500°F to observe the fatigue life of samples with different surface roughness. - **Data Analysis**: The relationship between surface roughness and fatigue life was established using the Coffin-Manson-Basquin and Ramberg-Osgood equations. ### Key Findings - **Impact of Surface Roughness**: Samples with rough surfaces exhibited significant stress concentration due to deeper valleys, leading to a notable reduction in fatigue life. - **Model Validation**: The proposed analytical model successfully predicted the fatigue life of Hastelloy X components manufactured by L-PBF under high-temperature conditions, with a maximum deviation of 2% (for vertically printed rough samples) and 10% (for 30° inclined printed rough samples) from the experimental results. ### Conclusion The study successfully developed an analytical method to accurately predict the fatigue life of Hastelloy X components manufactured by L-PBF based on their surface roughness under high-temperature conditions. This method provides important theoretical support for the application of complex L-PBF manufactured components in high-temperature environments.

Surface roughness-informed fatigue life prediction of L-PBF Hastelloy X at elevated temperature

An Approach to Estimate the Low Cycle Fatigue Probabilistic Curves of PBF-LB/M 316L Steel from Small Size Datasets Using the Remora Optimization Algorithm

Effect of Surface Modification on the High Temperature Low Cycle Fatigue Performance of LPBF 316L Austenitic Steel

High-temperature Oxidation Behavior of AlCoCrCuFeNi High-Entropy Alloy by Selective Laser Melting

High-temperature high-cycle fatigue performance and machine learning-based fatigue life prediction of additively manufactured Hastelloy X

A fatigue life model accounting for the combined effect of surface roughness and microstructure: Application to SLM fabricated Hastelloy-X

Investigating the deformation and microstructural evolution of laser powder-bed fusion of Hastelloy X during high temperature fatigue loading

Surface condition driven fatigue performance of laser powder bed fusion H13 steel

An Experimentally Informed Computational Framework for Investigating the Role of Surface Roughness on High Cycle Fatigue Life of LPBF IN718

Creep-fatigue Properties and Deformation Mechanism of 316L Steel Fabricated by Laser Powder Bed Fusion (PBF-LB/M)

Analysing the effect of defects on stress concentration and fatigue life of L-PBF AlSi10Mg alloy using finite element modelling

Fatigue life prediction of additively manufactured AlSi10Mg based on surface roughness and residual stress

Fatigue Characterization and Modeling of Additively Manufactured Hastelloy-X Superalloy

On the effect of laser powder-bed fusion process parameters on quasi-static and fatigue behaviour of Hastelloy X: A microstructure/defect interaction study

Room and elevated temperature tensile and fatigue behaviour of additively manufactured Hastelloy X

Defect-related strain-controlled high-temperature fatigue behavior in additive manufacturing Hastelloy X assisted with ultrasonic micro-forging treatment

Influence of LPBF-Surface Characteristics on Fatigue Properties of Scalmalloy®

X-ray imaging of defect population and the effect on high cycle fatigue life of laser additive manufactured Ti6Al4V alloys

High-temperature high cycle fatigue performance of laser powder bed fusion fabricated Hastelloy X: Study into the microstructure and oxidation effects

Impact of Surface and Pore Characteristics on Fatigue Life of Laser Powder Bed Fusion Ti-6Al-4V Alloy Described by Neural Network Models

Fatigue crack growth in additively manufactured Hastelloy X - Influences of crack orientation and post-fabrication treatments