Abstract:As a metallic material with lightweight and high specific strength, magnesium alloy has excellent application prospects. However, the rapid corrosion rate and localized corrosion behavior of magnesium alloys limit the practical application in the automobile industry. In this study, to improve the corrosion resistance of AZ91 alloy, the film of different concentrations containing zirconium (AZR0, AZR5, AZR10, AZR15) was prepared on the surface of AZ91 alloy by micro-arc oxidation technology in the Na 2 SiO 3 -Na 3 PO 4 system. Furthermore, the influence of electrolyte composition on the corrosion resistance of the MAO film was systematically investigated. The experimental results revealed that the ZrSiO 4 particles added in the electrolyte could enter into the MAO film and ZrSiO 4 particles were also decomposed into ZrO 2 and Mg 2 Zr 5 O 11 in the process of micro-arc oxidation. More importantly, the formation of micro-cracks and other defects in the film could be reduced after this process. The addition of 15 g l −1 ZrSiO 4 in the electrolyte was contributed to the best comprehensive properties of MAO-processed AZ91 specimens, including improved Vickers hardness of 167.16 Hv, Young’s modulus of 652 MPa, and enhanced corrosion resistance ( R P = 9.82 × 10 5 Ω cm 2 ). This approach could provide the approach for developing Mg-based materials with high anticorrosion in industrial fields.

Corrosion behavior of as-cast AZ91 magnesium alloy with VN particle additions in NaCl solution

Influence of Trace As Content on the Microstructure and Corrosion Behavior of the AZ91 Alloy in Different Metallurgical Conditions

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Microstructure and Corrosion Behavior of the As-cast Mg-xAl (x=9%, 12%, 15%) Alloys

Effect of Calcium Content on Corrosion Resistance of Az61-1.2y Magnesium Alloys

INFLUENCE OF YTTRIUM AND GADOLINIUM ON CORROSION RESISTANCE OF AZS1 MAGNESIUM ALLOYS

The Corrosion Behaviours of AZ61 Magnesium Alloy with the Ca Addition

Evaluation of microstructural effects on corrosion behaviour of AZ91D magnesium alloy

In Vitro Corrosion of Mg-6zn-1mn-4sn-1.5nd/0.5y Alloys

Effect of ZrSiO4 Concentration on the Microstructure and Corrosion Resistance of MAO Coatings Formed on AZ91 Magnesium Alloy

Role of alloyed Al on the microstructure and corrosion behavior of as-cast dilute Mg-2Zn- x Al-0.5Ca alloys

Effect of grain refinement induced by wire and arc additive manufacture (WAAM) on the corrosion behaviors of AZ31 magnesium alloy in NaCl solution

Corrosion behaviors of Zr-Sn-Nb alloys: Influence of different concentration dissolved oxygen environment and trace V element on the anti-corrosion properties

INFLUENCE OF YTTRIUM AND GADOLINIUM ON CORROSION RESISTANCE OF AZ81 MAGNESIUM ALLOYS

Influence of Yttrium Addition on the Corrosion Behaviour of As-Cast Mg–8Li–3Al–2Zn Alloy

Corrosion Behavior of Mg-Zn-Y-Zr Alloys in Nacl Solution

Influences of Ca and Y Addition on the Microstructure and Corrosion Resistance of Vacuum Die-Cast AZ91 Alloy

Influence of β-Mg 17 Al 12 and Al-Mn intermetallic compounds on the corrosion behaviour of cast and solution treated Mg-Al-Zn-Mn alloys

Microstructure, Mechanical Properties and Corrosion Behaviors of Al–Li–Cu–Mg–Ag–Zn Alloys

Investigating the corrosion behavior of as‐cast Mg‐Zn‐Ca alloys with the same Zn/Ca atomic ratio by in situ observation

TiCN Nanoparticle-Induced Corrosion Inhibition Mechanisms of AZ91 Alloy